LubrizolPellethane® 2363-90A Thermoplastic Polyurethane Elastomer
Thermoplastic Polyurethane, Elastomer, Ether Grade
Lubrizol (former Noveon)
产品说明：
Feature: USP Class VI
Available in Americas, Europe, Middle East, Africa, India andAsia
Dataprovided by Lubrizol
Lubrizol acquired the Pellethane product line from Dow in 2009.
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| 线性成型收缩率,Flow | 0.0050 - 0.0060 cm/cm | 0.0050 - 0.0060 in/in | ASTM D955 |
| 线性成型收缩率，横向 | 0.0050 - 0.0060 cm/cm | 0.0050 - 0.0060 in/in | ASTM D955 |
| 熔体流动速率 | 30 g/10 min @Load 1.20 kg, Temperature 224 °C | 30 g/10 min @Load 2.65 lb, Temperature 435 °F | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 A) | 90 | 90 | ASTM D2240 |
| 极限抗拉强度 | 40.3 MPa | 5850 psi | ASTM D412 |
| 伸长率 (断裂) | 500 % | 500 % | ASTM D412 |
| 50% Modulus | 0.00830 GPa | 1.20 ksi | ASTM D412 |
| 模量 | 0.0117 GPa | 1.70 ksi | ASTM D412 |
| 300％模量 | 0.0207 GPa | 3.00 ksi | ASTM D412 |
| 弯曲模量 | 0.0758 GPa | 11.0 ksi | ASTM D790 |
| 撕裂强度 | 100 kN/m | 571 pli | Die C; ASTM D624 |
| 泰伯磨损，毫克/1000次 | 10 | 10 | H22 Wheel, 1000g; ASTM D1044 |
| 压缩变形 | 25 % @Temperature 25.0 °C, Time 79200 sec | 25 % @Temperature 77.0 °F, Time 22.0 hour | ASTM D395, Method B |
| 30 % @Temperature 70.0 °C, Time 79200 sec | 30 % @Temperature 158 °F, Time 22.0 hour | ASTM D395, Method B | |
| Tensile Set | 30 % | 30 % | Elongation set after break; ASTM D412 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | 157 µm/m-°C @Temperature -80.0 - -30.0 °C | 87.2 µin/in-°F @Temperature -112 - -22.0 °F | ASTM D696 |
| 维卡软化温度 | 110 °C | 230 °F | 120°C.hr, 9.8N; ASTM D1525 |
| 玻璃化转变温度，Tg | -30.0 °C | -22.0 °F |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 204 - 221 °C | 399 - 430 °F | Molding |
| 模具温度 | 16.0 - 60.0 °C | 60.8 - 140 °F | |
| 干燥温度 | 88.0 - 104 °C | 190 - 219 °F | air dew point <-40°C |