Evatane®28-800
Ethylene Vinyl Acetate Copolymer
Arkema
产品说明：
EVATANE® 28-800 is a random copolymer of Ethylene and VinylAcetate made by high-pressure radicalar polymerization process.
The high Vinyl Acetate content of EVATANE® 28-800 brings softness,flexibility and polarity. EVATANE® 28-800 is compatible with mosttackifying resins and waxes. Combined with a high fluidity, it isan efficient and easy handling product for hot melt adhesivesformulations. EVATANE® 28-800 delivers high cohesive strength withmost fillers and may be used to produce masterbatches. It can alsobe used as a viscosity modifier for various EVA based compoundssuch as HFFR formulations for wires and cables.
物性信息：
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 形式 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 (23°C) | 0.950 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 700 到 900 | g/10 min | ASTM D1238, ISO 1133 |
| 醋酸乙烯含量 | 30.0 到 32.0 | wt% | 内部方法 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 A) | 60 | ASTM D2240, ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 (断裂) | 3.00 | MPa | ASTM D638, ISO 527-2 |
| 伸长率 (断裂) | 400 到 600 | % | ASTM D638, ISO 527-2 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | < 40.0 | °C | ISO 306/A, ASTM D1525 1 |
| 熔融温度 | 63.0 | °C | ISO 11357-3 |
| Ring and Ball Softening Point 2 | 80 | °C | ASTM E28 |
EVA熔点很低，我公司有低熔点EVA树脂，熔点50度，熔点60度，熔点70度，熔点80度，熔点100度，以及不同软硬度的EVA材料。
塑料介绍：
（一）EVA具有很好的弹性和抗压缩变形性能，具有橡胶般的弹性，透明度和光泽度很好，耐油抗化学腐蚀性好，抗老化和臭氧；可以符合食品级环保要求，很好配颜色。
（二）我公司有注塑级EVA，挤出EVA，挤出吸塑EVA，押出EVA，热熔胶用EVA，油墨涂料用EVA（溶解于环-己-酮，丙-酮等溶剂里)，流延膜用EVA，涂覆用EVA，压延EVA，发泡级，热成型用，中空吹塑EVA，吹瓶EVA，以及电线电缆，低烟无卤电缆材料。
（三）EVA有比聚乙-烯（LDPE，HDPE，LLDPE）更好的弹性，有比聚丙烯PP更好的柔韧性，不会出现应力发白，抗应力泛白等现象。