Evatane®24-03
Ethylene Vinyl Acetate Copolymer
Arkema
产品说明：
EVATANE® 24-03 is a random copolymer of Ethylene and VinylAcetate made by high-pressure radicalar polymerization process.
The high Vinyl Acetate content of EVATANE® 24-03 brings softness,flexibility and polarity. EVATANE® 24-03 delivers high cohesivestrength with most fillers and can be used to produce masterbatchesor HFFR compounds, and can be used as an additive for bitumenmodification. EVATANE® 24-03 is also suitable for film (cast orblown) extrusion, and exhibits good adhesion onto PE, PS andpolyesters.
物性信息：
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 (23°C) | 0.940 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 2.5 到 3.5 | g/10 min | ASTM D1238, ISO 1133 |
| 醋酸乙烯含量 | 23.0 到 25.0 | wt% |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 A) | 83 | ASTM D2240, ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 (断裂) | 27.0 | MPa | ASTM D638, ISO 527-2 |
| 伸长率 (断裂) | 600 到 900 | % | ASTM D638, ISO 527-2 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | 46.0 | °C | ISO 306/A, ASTM D1525 1 |
| 熔融温度 | 80.0 | °C | ISO 11357-3 |
| Ring and Ball Softening Point 2 | 183 | °C | ASTM E28 |
EVA中，VA含量5%-40%左右，EVA有很好的弹性和柔韧度，耐低温抗冲击性能好，可以在寒冷低温零下40-60度使用；热封性能好，熔点低；我公司又VA含量3%，VA含量5%，VA含量8%，VA含量10%，VA含量12%，VA含量15%，VA含量18%，VA含量20%，VA含量25%，VA含量30%，VA含量40%的EVA材料。
EVA用于薄膜，可以提高薄膜的抗穿刺性能，做PP和PE塑料的增韧剂，发泡鞋材，鞋底，管子，汽车油管，型材，包装膜，热熔胶，玩具，色母载体，低烟无卤电线电缆，改性用，儿童玩具，瑜伽垫，塑料地板，汽车配件，发泡产品，拼豆豆，凉鞋，洞洞鞋，油墨，涂料，胶水。