阻燃级PA6T 日本三井化学 CRLEN™C430N
聚酰胺6T
30%玻璃纤维增强材料
MitsuiChemicals, Inc.
产品说明:
ARLEN™C430N by Mitsui Chemicals is a modified polyamide 6T reinforcedwith 30% glass fiber. Possesses high dimensional stability, highmelting point, high rigidity and minimum water absorption. Exhibitsgood chemical and heat resistance. Is suitable for processing byinjection molding. ARLEN™ C430N is recommended for electrical &electronic parts including connectors, jacks, switches and powersupply terminals. Complies with UL 94 V-0 flame rating.
Features:
Highdimensional stability
Highmelting point
Highrigidity
Minimumwater absorption
Goodchemical and heat resistance
Flameretardant
Applications:
Electricaland electronic parts including: connectors, jacks, switches, andpower supply terminals.
C430N物性表
| 基本信息 | |
|---|---|
| 填料/增强材料 |
|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.66 | g/cm3 | ASTMD792 |
| 收缩率 | ASTMD955 | ||
| 流动 | 0.30 | % | ASTMD955 |
| 横向流动 | 0.70 | % | ASTMD955 |
| 吸水率 (23°C,24 hr, 65%r.h) | 2.0 | % | ASTMD570 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 (M级) | 95 | ASTMD785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | 170 | MPa | ASTMD638 |
| 伸长率 (断裂) | 3.0 | % | ASTMD638 |
| 弯曲模量 | 11400 | MPa | ASTMD790 |
| 弯曲强度 | 250 | MPa | ASTMD790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 | 85 | J/m | ASTMD256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 (1.8MPa, 未退火) | 295 | °C | ASTMD648 |
| 玻璃转化温度 | 85.0 | °C | |
| 熔融温度 | 310 | °C | |
| 线形热膨胀系数 | ASTME831 | ||
| 流动 | 1.2E-5 | cm/cm/°C | ASTME831 |
| 横向 | 9.2E-5 | cm/cm/°C | ASTME831 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.0E+15 | ohms·cm | ASTMD257 |
| 介电强度 | 26 | kV/mm | ASTMD149 |
| 介电常数 (1MHz) | 4.00 | ASTMD150 | |
| 耗散因数 (1MHz) | 0.013 | ASTMD150 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UL阻燃等级 | V-0 | UL94 |
30N 玻纤增强 低吸水 耐化学性电气应用