HANWHA EVA2050
Ethylene Vinyl Acetate Copolymer
Hanwha Chemical
产品说明：
HANWHA EVA 2050 is manufactured by DOW tubular high pressureprocess and designed for variety of film application such asmultiplayer agricultural film. EVA 2050 has well balanced propertyof high clarity, mechanical property and processability.
物性信息：
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.931 | g/cm³ | ASTM D1505 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| 醋酸乙烯含量 | 12.0 | wt% |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 (断裂) | 19.6 | MPa | ASTM D638 |
| 伸长率 (断裂) | 780 | % | ASTM D638 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 60 | µm | |
| 抗张强度 | ASTM D882 | ||
| MD : 断裂, 60µm | 27.9 | MPa | ASTM D882 |
| TD : 断裂, 60µm | 26.5 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂, 60µm | 370 | % | ASTM D882 |
| TD : 断裂, 60µm | 680 | % | ASTM D882 |
| 落锤冲击 (60 µm) | > 400 | g | ASTM D1709 |
| Tensile Tear Strength | ASTM D1004 | ||
| MD : 60.0µm | 73.5 | kN/m | ASTM D1004 |
| TD : 60.0µm | 78.5 | kN/m | ASTM D1004 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 脆化温度 | < -76.0 | °C | ASTM D746 |
| 维卡软化温度 | 72.0 | °C | ASTM D1525 |
| 熔融峰值温度 | 96.0 | °C | 内部方法 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 雾度 (60.0 µm) | 1.5 | % | ASTM D1003 |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 熔体温度 | 140 到 170 | °C |