IXEF PARA 1022/9008 索尔维

IXEF PARA 1022/9008 索尔维-->PARA-GF50< 阻燃等级: HB 缺口冲击: 11.22kJ/m² 符合规定: UL材料特性: 良好的外观 • 超高刚性 • 耐化学性 • 抗蠕变 • 通用级 • 尺寸稳定 • 良好的消毒性• 高流动性 • 高强度 • 低吸水率

材料用途: 手机 • 电器用具 • 汽车领域的应用 • 汽车内部零件 • 电气元件 • 家具 • 高光应用 • 医疗器械 •体育用品应用 • 外科器械汽车规格: ASTM D6779 PA111G50 • BOSCH N28 BN05-OX1Color:0008 Natural • BOSCH N28 BN05-OX1 Color:9008 Black • GMGM7001M PAMXD6(A4,A22,A64,BA651,G30,MS1700,NS335)Color:9008 Black •GM GM7001M PAMXD6(A4,A22,A64,BA751,G30,MS1700,NS350)Color:0008Natural

注射说明

Hot runners: 250°C to 260°C (482°C to 500°F)StorageIxef®compounds are shipped in moisture-resistant packages at moisturelevels according to specifications. Sealed, undamaged bags shouldbe preferably stored in a dry room at a maximum temperature of 50°C(122°F) and should be protected from possible damage. If only aportion of a package is used, the remaining material should betransferred into a sealable container. It is recommended that Ixef®resins be dried prior to molding following the recommendationsfound in this datasheet and/or in the Ixef® processingguide.DryingThe material as supplied is ready for molding withoutdrying. However, If the bags have been open for longer than 24hours, the material needs to be dried. When using a desiccant airdryer with dew point of -28°C (-18°F) or lower, these guidelinescan be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C(212°F), or 1-7 hours at 80°C (176°F).Injection MoldingIxef 1022compound can be readily injection molded in most screw injectionmolding machines. A general purpose screw is recommended, withminimum back pressure.The measured melt temperature should be about280°C (536°F), and the barrel temperatures should be around 250 to260°C (482 to 500°F) in the rear zone, gradually increasing to 260to 290°C (500 to 554°F) in the front zone. If hot runners are used,they should be set to 250 to 260°C (482 to 500°F).To maximizecrystallinity, the temperature of the mold cavity surface must beheld between 120 and 140°C (248 and 284°F). Molding at lowertemperatures will produce articles that may warp, have poor surfaceappearance, and have a greater tendency to creep. Set injectionpressure to give rapid injection. Adjust holding pressure and holdtime to maximize part weight. Transfer from injection to holdpressure at the screw position just before the part is completelyfilled (95-99%).