POM 美国杜邦 507 增强级 抗紫外线 耐高温 聚甲醛#赛钢
产品参数
性能项目试验条件[状态]测试方法测试数据数据单位基本性能密度ASTM D-7921.42
物理性能吸水量Equil.50%R.h.+73℉(+23℃)ASTMD-5700.22%扩散因数+73℉(+23℃)106HzASTM D-1500.005
吸水量24hrs浸泡+73℉(+23℃)ASTM D-5700.25%吸水量浸泡均衡点+73℉(+23℃)ASTMD-5700.90%机械性能挠曲系数-55℃在25℃下3930MPa挠曲系数+122℃在25℃下620MPa挠曲系数+23℃在25℃下2830MPa伸张强度+158℉ASTMD-6386.9MPsiIZOD冲击强度+23℃ASTM D-25674.7j/m弹性系数+73℉ASTMD-638450MPsi断裂时之拉力伸张度-68℉(-55℃)ASTM D-63813%拉力冲击抵抗力+23℃ASTMD-1822200kj/m2压缩应力+23℃@1%Def.ASTMD-69535.9MPa摩擦系数+73℉(+23℃)静态ThrustWasherTest30.20
IZOD冲击强度+73℉ASTM D-2561.4ft.lb/in伸张强度-68℉ASTM D-63814.7MPsi洛氏硬度
ASTM D-785M94,R120
剪力+73℉ASTM D-7329.5MPsiIZOD冲击强度40℃ASTM D-25664.1j/m伸张强度+23℃ASTMD-63868.9MPa弯曲疲劳忍耐限度+73℉ASTM D-6714.5MPsiIZOD冲击强度-40℉ASTMD-2561.2ft.lb/in断裂时之拉力伸张度+158℉(+70℃)ASTM D-638220%伸张强度-55℃ASTMD-638101MPa无切口冲击程度+23℃ASTM D-2561280j/m伸张强度+70℃ASTMD-63847.5MPa挠曲系数-68℉在25℃下570MPsi断裂时之拉力伸张度+73℉(+23℃)ASTMD-63840%弹性系数+23℃ASTM D-6383100MPa伸张强度+212℉ASTMD-6385.2MPsi压缩应力+73℉@1% Def.ASTMD-6955.2MPsi挠曲系数+70℃在25℃下1585MPa挠曲系数+212℉在25℃下135MPsi伸张强度+100℃ASTMD-63835.9MPa断裂时之拉力伸张度+212℉(+100℃)ASTM D-638>260%弯曲降服强度+23℃ASTMD-79097.2MPa摩擦系数+73℉(+23℃)动态ThrustWasherTest30.35
压缩应力+73℉@10% Def.ASTM D-69518.0MPsi断裂时之拉力伸张度+250℉(+122℃)ASTMD-638>260%弯曲降服强度+73℉ASTMD-79014.1MPsi负载下之变形2000psi@+122℉(14Mpa@50℃)ASTMD-6210.5%伸张强度+73℉ASTM D-63810.0MPsi无切口冲击程度+73℉ASTMD-25624ft.lb/in伸张强度+250℉ASTM D-6383.8MPsi剪力+23℃ASTMD-73265.5MPa伸张强度+122℃ASTM D-63826.2MPa压缩应力+23℃@10% Def.ASTMD-695124MPa挠曲系数+158℉在25℃下230MPsi挠曲系数+100℃在25℃下90MPsi弯曲疲劳忍耐限度+23℃ASTMD-67131.0MPa挠曲系数+73℉在25℃下410MPsi拉力冲击抵抗力+73℉ASTMD-1822100ft.lb/in2电气性能绝缘强度Short Time,2.3mmASTMD-14919.7MV/m绝缘系数+73℉(+23℃)102to106HzASTMD-1503.7
电阻系数+73℉(+23℃)0.2%H2OASTMD-2571015ohm-cm绝缘强度Short Time,90 milsASTMD-149500V/mil电弧抵抗力120mil(3.1mm)ASTM D-495220notrackingSec.热性能熔点
ASTM D-2133347℉线性热膨胀系数+85 to +140℉ASTMD-6966.810-5in/in.℉可燃烧性
UL-9494HB
热变形温度0.5MPaASTM D-648172℃热传导系数BTU-in/hr
2.6
线性热膨胀系数+60 to +104℃ASTM D-69613.710-5m/m.℃线性热膨胀系数-40to +29℃ASTM D-69610.410-5m/m.℃线性热膨胀系数-40 to +85℉ASTMD-6965.810-5in/in.℉热传导系数W/mk
0.37
热变形温度1.8MPaASTM D-648136℃热变形温度264psiASTM D-648277℉线性热膨胀系数+29 to+60℃ASTM D-69612.210-5m/m.℃热变形温度66psiASTMD-648342℉线性热膨胀系数+140 to +220℉ASTMD-6967.610-5in/in.℉线性热膨胀系数+104 to +150℃ASTMD-69614.910-5m/m.℃线性热膨胀系数+220 to +300℉ASTMD-6968.310-5in/in.℉熔点
ASTM D-2133175℃
聚甲醛是一种表面光滑、有光泽的硬而致密的材料，淡黄或白色，薄壁部分呈半透明。燃烧特性为容易燃烧，离火后继续燃烧，火焰上端呈黄色，下端呈蓝色，发生熔融滴落，有强烈的刺激性甲醛味、鱼腥臭。聚甲醛为白色粉末，一般不透明，着色性好，比重1.41-1.43克/立方厘米，成型收缩率1.2-3.0%，成型温度170-200℃，干燥条件80-90℃2小时。POM的长期耐热性能不高，但短期可达到160℃，其中均聚POM短期耐热比共聚POM高10℃以上，但长期耐热共聚POM反而比均聚POM高10℃左右。可在-40℃～100℃温度范围内长期使用。POM极易分解，分解温度为280度，分解时有刺激性和腐蚀性气体发生。故模具钢材宜选用耐腐蚀性的材料制作。