PC 德国科思创(拜耳) 6555 阻燃性 高耐热 抗冲击 汽车部件应用
PC 德国拜耳 6555阻燃级物性认证数据表性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度)ASTM D638/ISO 52765kg/cm2(MPa)[Lb/in2]断裂伸长率
ASTM D638/ISO 527
%拉伸模量
ASTM D638/ISO 5272400kg/cm2(MPa)[Lb/in2]拉伸屈服伸长率(延伸率)
ASTM D638/ISO 5276%拉伸断裂伸长率(延伸率)
ASTM D638/ISO 527>50%弯曲模量(弯曲弹性率)
ASTM D790/ISO 178
kg/cm2(MPa)[Lb/in2]弯曲强度
ASTM D790/ISO 178
kg/cm2(MPa)[Lb/in2]洛氏硬度
ASTM D785
IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 17985kg·cm/cm(J/M)ft·lb/in1/4"-30℃ASTM D256/ISO 17915kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO179
kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ (缺口)ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in-30℃(缺口)ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in23℃(无缺口)ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in-30℃(无缺口)ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in物性性能比重(密度)
ASTM D792/ISO 11831200
成型收缩率
ASTM D9550.6-0.8%熔融指数(流动系数)200℃/5kgASTM D1238/ISO 1133
g/10min220℃/10kgASTM D1238/ISO 113310g/10min吸水率 23℃/24H
ASTM D570/ISO 620.35%热性能热变形温度退火ASTM D648/ISO 75
℃(℉)未退火ASTM D648/ISO 75
℃(℉)维卡软化点
ASTM D1525/ISO R306144℃(℉)熔点
-
℃(℉)燃烧性(率)
UL94V-2
线性膨胀系数
ASTM D696/ISO 113590.7mm/mm.℃电气性能介电常数100HZASTM D150/IEC602503.0
1MHZASTM D150/IEC 602503.0
介电损耗100HZASTM D150/IEC 6025010
1MHZASTM D150/IEC 6025090
体积电阻率
ASTM D257/IEC 60093
Ω.cm表面电阻率
ASTM D257/IEC 60093
Ω耐电弧性
ASTM D495/IEC 60112
光学性能折射率
ASTM D542/ISO 4891.586
透光率
ASTM D1003/ISO 1346888%模糊系数(Haze)
ISO 14782
%加工条件干燥条件
加工温度射嘴
℃料筒前段
℃料筒中段
℃料筒后段
℃熔体温度
℃模具温度
℃压力注塑压力
Mpa保压压力
Mpa背压
Mpa螺杆转速
rpm其他备注
颜色
特性
用途
非增强阻燃品级
牌号
特点和用途
6385
易流动注射级,易脱模。V-0级/1.5mm。不透明,应用领域涉及电气工程、照明工程、信息工程和交通系统
6555
6557
中粘度注射品级,易脱模,V-0/3.0mm级。其中6557为防紫外线稳定,有透明、半透明和不透明色,应用领域涉及电气工程、照明工程、信息工程和交通系统
6465
6485
中粘度注射品级,易脱模,V-0,不透明,应用领域涉及电气工程、照明工程、信息工程和交通系统
6870
高粘度带支链的挤出注射品级,V-0级/1.5mm,只有透明色,应用领域涉及电气工程、照明工程
聚碳酸酯(简称PC)是分子链中含有碳酸酯基的高分子聚合物,根据酯基的结构可分为脂肪族、芳香族、脂肪族-芳香族等多种类型。其中由于脂肪族和脂肪族-芳香族聚碳酸酯的机械性能较低,从而限制了其在工程塑料方面的应用。目前芳香族聚碳酸酯获得了工业化生产。由于聚碳酸酯结构上的特殊性,现已成为五大工程塑料中增长速度快的通用工程塑料。
成分聚碳酸酯是一种强韧的热塑性树脂,其名称来源于其内部的co3基团。可由双酚A和氧氯化碳(COCl2)合成。现较多使用的方法为熔融酯交换法(双酚A和碳酸二苯酯通过酯交换和缩聚反应合成)。