Queo™0210
Ethylene-based Plastomer
Borealis AG
产品说明：
Queo™ 0210 is an ethylene based octene plastomer, produced in asolution polymerisation process using a metallocene catalyst.
Queo 0210 is an effective and versatile blend partner for otherpolyolefin polymers, providing :
Excellent PP compatibility
High flexibility
Outstanding toughness
Excellent low-temperature flex-cracking resistance
High clarity
Applications:
Demonstrated applications include :
Household consumer goods
High clarity PP moulded goods
Closures
Masterbatch carrier
Wire and cable compounds
Highly filled compounds
Extrusion coated structures
物性信息：
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.902 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| 抗环境应力开裂 | > 1000 | hr | ASTM D1693B |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 38 | ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力 (断裂) | 14.0 | MPa | ISO 527-2/5A |
| 拉伸应变 (断裂) | 930 | % | ISO 527-2/5A |
| 弯曲模量 | 65.0 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 (23°C) | 无断裂 | ISO 180/1A |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 脆化温度 | < -76.0 | °C | ASTM D746 |
| 维卡软化温度 | 75.0 | °C | ISO 306/A |
| 溶融温度（DSC） | 97.0 | °C | ISO 11357 |
| 挤出 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 内缩量 - 100 m/min | 68.0 | mm | 内部方法 |
| 下拉 | 490 | m/min | 内部方法 |