Polyamide 66
Ascend Performance Materials Operations LLC
产品说明：
Vydyne 21SPC is a general-purpose PA66 resin. Available innatural color. It is designed principally for injection-moldingfabrication. This resin offers a well balanced combination ofengineering properties characterized by high strength; rigidity;good toughness; high melt point; good surface lubricity; abrasionresistance; and resistance to many chemicals, machine and motoroils, solvents and gasoline.
Vydyne 21SPC permits production of molded parts with good initialcolor plus good property and color retention when using regrind.This resin is recognized by Underwriters Laboratories and conformsto the requirements of many industrial, federal and militaryspecifications for premium-quality, general-purpose PA66resins.
Internally and externally lubricated for improved machine feed andexceptional mold release. Vydyne 21SPC is intended for use inhigh-productivity applications. In many applications, the moldingcycle can be reduced because parts may be removed from the cavityat higher temperatures. In difficult molds where parts have atendency to stick in the cavity, Vydyne 21SPC can reduce oreliminate the need for mold release sprays. Critical molded-partdimensions should be checked against specifications beforeimplementing shorter molding cycles on a routine productionbasis.
Typical Applications/End Uses:
Vydyne 21SPC has been used in many molding applications such asterminal blocks, bearings, bushings, cams, electrical connectorsand housings, electrical cable ties/tie straps and many otherhardware and general industrial parts.
物性信息：
基本信息黄卡编号
E70062-249058
添加剂润滑剂
特性刚性，高
高强度
抗溶剂性
快的成型周期
良好耐磨损性
耐化学性良好
耐汽油性
耐油性能
韧性良好
润滑
通用
脱模性能良好
用途衬套
工业应用
连接器
凸轮
外壳
轴承
机构评级ASTM D 4066 PA0111
ASTM D 6779 PA0111
FDA 21 CFR 177.1500
FED L-P-410A
MIL M-20693B
RoHS 合规性RoHS 合规
UL文件号E70062
外观自然色
形式粒子
加工方法注射成型
多点数据Isothermal Stress vs. Strain (ISO 11403-1)
物理性能干燥调节后的单位制测试方法密度1.14--g/cm³ISO 1183收缩率ISO 294-4 垂直流动方向: 23°C, 2.00 mm1.7--%ISO294-4 流动方向 :23°C, 2.00 mm1.8--%ISO 294-4吸水率
ISO 62 23°C, 24hr1.2--%ISO 62 平衡, 23°C, 50% RH2.4--%ISO 62室外适用性f2--
UL 746C机械性能干燥调节后的单位制测试方法拉伸模量 (23°C)31001400MPaISO 527-2拉伸应力
ISO 527-2 屈服,23°C82.055.0MPaISO527-2 断裂,23°C55.045.0MPaISO 527-2拉伸应变 (屈服,23°C)5.025%ISO 527-2标称拉伸断裂应变 (23°C)25> 50%ISO 527-2弯曲模量 (23°C)29001500MPaISO 178弯曲强度 (23°C)80.050.0MPaISO 178泊松比0.40--
ISO 527冲击性能干燥调节后的单位制测试方法简支梁缺口冲击强度
ISO 179/1eA -30°C5.07.0kJ/m²ISO179/1eA 23°C6.020kJ/m²ISO 179/1eA简支梁无缺口冲击强度
ISO 179/1eU -30°C无断裂无断裂
ISO 179/1eU 23°C无断裂无断裂
ISO 179/1eU悬壁梁缺口冲击强度
ISO 180 -30°C5.07.0kJ/m²ISO180 23°C6.020kJ/m²ISO 180热性能干燥调节后的单位制测试方法热变形温度
0.45 MPa,未退火200--°CISO75-2/B 1.8 MPa,未退火70.0--°CISO 75-2/A熔融温度260--°CISO 11357-3线形热膨胀系数
ISO 11359-2 流动 :23 到 55°C1.0E-4--cm/cm/°CISO11359-2 横向 : 23到 55°C1.0E-4--cm/cm/°CISO 11359-2RTI Elec
UL 746 0.400mm130--°CUL 746 0.710 mm130--°CUL746 1.50mm130--°CUL 746 3.00 mm130--°CUL 746RTI Imp
UL 746 0.400mm75.0--°CUL 746 0.710 mm75.0--°CUL746 1.50mm75.0--°CUL 746 3.00 mm75.0--°CUL 746RTI
UL 746 0.400mm75.0--°CUL 746 0.710 mm85.0--°CUL746 1.50mm85.0--°CUL 746 3.00 mm85.0--°CUL746电气性能干燥调节后的单位制测试方法体积电阻率 (0.750mm)1.0E+13--ohms·cmIEC 60093介电强度 (1.00 mm)26--kV/mmIEC 60243耐电弧性 (3.00 mm)PLC 5--
ASTM D495漏电起痕指数 (3.00mm)600--VIEC 60112高电弧燃烧指数(HAI)
UL 746 0.400mmPLC 1--
UL 746 0.710mmPLC 0--
UL 746 1.50mmPLC 0--
UL 746 3.00mmPLC 0--
UL 746高电压电弧起痕速率 (HVTR)PLC 0--
UL 746热丝引燃 (HWI)
UL 746 0.400mmPLC 4--
UL 746 0.710mmPLC 4--
UL 746 1.50mmPLC 3--
UL 746 3.00mmPLC 2--
UL 746可燃性干燥调节后的单位制测试方法UL 阻燃等级
UL 94 0.400mmV-2--
UL 94 0.710mmV-2--
UL 94 1.50mmV-2--
UL 94 3.00mmV-2--
UL 94灼热丝易燃指数
IEC 60695-2-12 0.400 mm960--°CIEC60695-2-12 0.710mm960--°CIEC60695-2-12 1.50mm960--°CIEC60695-2-12 3.00mm960--°CIEC 60695-2-12热灯丝点火温度
IEC 60695-2-13 0.400 mm825--°CIEC60695-2-13 0.710mm850--°CIEC60695-2-13 1.50mm850--°CIEC60695-2-13 3.00mm850--°CIEC 60695-2-13极限氧指数25--%ISO 4589-2注射干燥单位制
干燥温度< 70.0°C
干燥时间1.0 到 3.0hr
建议的Zui大回制料比例50%
料筒后部温度260 到 280°C
料筒中部温度270 到 285°C
料筒前部温度280 到 290°C
射嘴温度280 到 300°C
加工（熔体）温度285 到 300°C
模具温度65.0 到 95.0°C