DuPontPerformance Polymers Zytel® ST801 NC010A Nylon 66 (UnverifiedData**)
Nylon 66, Impact Grade
DuPont Performance Polymers
产品说明：
Super Toughened Polyamide 6
ZytelST801 is an unreinforced super tough polyamide 66 for injectionmolding and extrusion. It offers outstanding break resistance overa wide temperature and humidity range and high productivity.
Information provided by DuPont Performance Polymers
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.08 g/cc | 0.0390 lb/in³ | DAM; ISO 1183 |
| 吸水率 | 6.7 % @Thickness 2.00 mm | 6.7 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 水分吸收 | 2.20 % @Thickness 2.00 mm | 2.20 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 线性成型收缩率,Flow | 0.017 cm/cm | 0.017 in/in | DAM; ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | 43.0 MPa | 6240 psi | 50%RH; ISO 527-1/-2 |
| 50.0 MPa | 7250 psi | DAM; ISO 527-1/-2 | |
| 伸长率 (断裂) | 32 % | 32 % | DAM; Nominal; ISO 527-1/-2 |
| >= 50 % | >= 50 % | 50%RH; Nominal; ISO 527-1/-2 | |
| 屈服伸长率 | 5.7 % | 5.7 % | DAM; ISO 527-1/-2 |
| 37 % | 37 % | 50%RH; ISO 527-1/-2 | |
| 拉伸模量 | 0.900 GPa | 131 ksi | 50%RH; ISO 527-1/-2 |
| 2.00 GPa | 290 ksi | DAM; ISO 527-1/-2 | |
| 剪切模量 | 0.0822 GPa @Temperature 150 °C | 11.9 ksi @Temperature 302 °F | DAM; Dynamic; ISO 11403-1 -2 |
| 0.1075 GPa @Temperature 110 °C | 15.59 ksi @Temperature 230 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| 0.2994 GPa @Temperature 60.0 °C | 43.42 ksi @Temperature 140 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| 0.6815 GPa @Temperature 10.0 °C | 98.84 ksi @Temperature 50.0 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| 0.7189 GPa @Temperature -20.0 °C | 104.3 ksi @Temperature -4.00 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| 0.9346 GPa @Temperature -50.0 °C | 135.6 ksi @Temperature -58.0 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| 简支梁无缺口冲击强度 | NB | NB | DAM; ISO 179/1eU |
| NB | NB | 50%RH; ISO 179/1eU | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | DAM; ISO 179/1eU | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 50%RH; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 8.00 J/cm² | 38.1 ft-lb/in² | DAM; ISO 179/1eA |
| 11.5 J/cm² | 54.7 ft-lb/in² | 50%RH; ISO 179/1eA | |
| 1.70 J/cm² @Temperature -30.0 °C | 8.09 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | |
| 1.80 J/cm² @Temperature -30.0 °C | 8.57 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |
| 拉伸蠕变模量(1 hr) | 1200 MPa @Time 3600 sec | 174000 psi @Time 1.00 hour | 50%RH; ISO 899-1 |
| 拉伸蠕变模量(1000 hr) | 750 MPa @Time 3.60e+6 sec | 109000 psi @Time 1000 hour | 50%RH; ISO 899-1 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | 50%RH; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DAM; IEC 60093 | |
| 表面电阻 | >= 1.00e+15 ohm | >= 1.00e+15 ohm | 50%RH; IEC 60093 |
| 介电常数 | 2.9 @Frequency 1.00e+6 Hz | 2.9 @Frequency 1.00e+6 Hz | DAM; IEC 60250 |
| 3.2 @Frequency 100 Hz | 3.2 @Frequency 100 Hz | DAM; IEC 60250 | |
| 3.6 @Frequency 1.00e+6 Hz | 3.6 @Frequency 1.00e+6 Hz | 50%RH; IEC 60250 | |
| 8.0 @Frequency 100 Hz | 8.0 @Frequency 100 Hz | 50%RH; IEC 60250 | |
| 介电强度 | 31.0 kV/mm | 787 kV/in | DAM; IEC 60243-1 |
| 39.0 kV/mm | 991 kV/in | 50%RH; IEC 60243-1 | |
| 耗散因数 | 0.0080 @Frequency 100 Hz | 0.0080 @Frequency 100 Hz | DAM; IEC 60250 |
| 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | DAM; IEC 60250 | |
| 0.055 @Frequency 1.00e+6 Hz | 0.055 @Frequency 1.00e+6 Hz | 50%RH; IEC 60250 | |
| 0.18 @Frequency 100 Hz | 0.18 @Frequency 100 Hz | 50%RH; IEC 60250 | |
| 相比耐漏电起痕指数(CTI) | 600 V | 600 V | DAM; IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 120 µm/m-°C | 66.7 µin/in-°F | DAM; ISO 11359-1/-2 |
| 线性热膨胀系数,横向流动 | 90.0 µm/m-°C | 50.0 µin/in-°F | DAM; ISO 11359-1/-2 |
| 熔融温度 | 263 °C | 505 °F | DAM; 10°C/min; ISO 11357-1/-3 |
| 载荷下热变形温度(0.46 MPa) | 132 °C | 270 °F | DAM; ISO 75-1/-2 |
| 载荷下热变形温度(1.8 MPa) | 64.0 °C | 147 °F | DAM; ISO 75-1/-2 |
| 玻璃化转变温度，Tg | 75.0 °C | 167 °F | DAM; 10°C/min; ISO 11357-1/-2 |
| 可燃性(UL94) | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 |
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | DAM; IEC 60695-11-10 | |
| Flame Spread | 26 mm/min @Thickness 1.00 mm | 1.0 in/min @Thickness 0.0394 in | ISO 3795 (FMVSS 302) |
| 极限氧指数 | 20 % | 20 % | DAM; ISO 4589-1/-2 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Emission of organic compounds | 38.4 µgC/g |