LG ChemicalAF312T ABS, Flame Retardant
Acrylonitrile Butadiene Styrene (ABS), Molded
LG Chemical
产品说明：
Feature: Injection Molding, Flame Retardant
Application: Electric/Electronic Applications (TV, Monitor Housing)IT/OA device
CASNo. 9003-56-9, 79-94-7 and 1309-64-4
Information provided by LG Chemical
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| 处理 | 0.010 | 0.010 | Injection Molding |
| 线性成型收缩率,Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0070 in/in @Thickness 0.126 in | ASTM D955 |
| 熔体流动速率 | 52 g/10 min @Load 10.0 kg, Temperature 220 °C | 52 g/10 min @Load 22.0 lb, Temperature 428 °F | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | 104 | 104 | ASTM D785 |
| 抗张强度(屈服) | 42.2 MPa @Thickness 3.20 mm | 6120 psi @Thickness 0.126 in | 50 mm/min; ASTM D638 |
| 伸长率 (断裂) | 25 % @Thickness 3.20 mm | 25 % @Thickness 0.126 in | 50 mm/min; ASTM D638 |
| 屈服伸长率 | >= 5.0 % @Thickness 3.20 mm | >= 5.0 % @Thickness 0.126 in | 50 mm/min; ASTM D638 |
| 拉伸模量 | 2.16 GPa @Thickness 3.20 mm | 313 ksi @Thickness 0.126 in | 1 mm/min; ASTM D638 |
| 弯曲强度 | 68.6 MPa @Thickness 6.40 mm | 9960 psi @Thickness 0.252 in | 15 mm/min; ASTM D790 |
| 弯曲模量 | 2.60 GPa @Thickness 6.40 mm | 377 ksi @Thickness 0.252 in | 15 mm/min; ASTM D790 |
| 悬壁梁缺口冲击强度 | 2.26 J/cm @Thickness 6.40 mm, Temperature 23.0 °C | 4.22 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F | ASTM D256 |
| 2.75 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 5.14 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 | |
| Izod Impact, Unnotched | 0.785 J/cm @Thickness 6.40 mm, Temperature -30.0 °C | 1.47 ft-lb/in @Thickness 0.252 in, Temperature -22.0 °F | ASTM D256 |
| 0.785 J/cm @Thickness 3.20 mm, Temperature -30.0 °C | 1.47 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F | ASTM D256 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | |
| 介电强度 | 30.0 kV/mm | 762 kV/in | |
| 相比耐漏电起痕指数(CTI) | 400 - 600 V | 400 - 600 V | |
| 热丝引燃 (HWI) | 15 - 30 sec @Thickness >=1.50 mm | 15 - 30 sec @Thickness >=0.0591 in | |
| 15 - 30 sec @Thickness >=2.00 mm | 15 - 30 sec @Thickness >=0.0787 in | ||
| 15 - 30 sec @Thickness >=2.50 mm | 15 - 30 sec @Thickness >=0.0984 in |