乙烯丙烯酸共聚物/美国陶氏5980I(EAA膜)
乙烯丙烯酸共聚物/美国陶氏5980I(EAA膜)
乙烯丙烯酸共聚物/美国陶氏5980I(EAA膜)
| 熔体流动速率 | 125℃/2.16kg | ASTM D-1238 | 14 | g/10min | |
| 熔体流动速率 | 190℃/2.16kg | ISO 1133 | 300 | g/10min | |
| 单体含量 | Internal Method | 20.5 | % | ||
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 300 | g/10min | |
| 熔体流动速率 | 125℃/2.16kg | ISO 1133 | 14 | g/10min | |
| 物理性能 | 比重 | ASTM D-792 | 0.958 | g/cm3 | |
| 比重 | ISO 1183 | 0.958 | g/cm3 | ||
| 机械性能 | 邵氏硬度 | Shore D | ASTM D-2240 | 50 | |
| 邵氏硬度 | Shore D | ISO 868 | 50 | ||
| 拉伸模量-2% Secant | Compression Molded | ASTM D-638 | 33.1 | MPa | |
| 拉伸模量-2% Secant | Compression Molded | ISO 527-2 | 33.1 | MPa | |
| 拉伸断裂强度 | Compression Molded | ASTM D-638 | 9.65 | MPa | |
| 拉伸断裂强度 | Compression Molded | ISO 527-2 | 9.65 | MPa | |
| 拉伸断裂伸长率 | Compression Molded | ASTM D-638 | 390 | % | |
| 拉伸断裂伸长率 | Compression Molded | ISO 527-2 | 390 | % | |
| 热性能 | 维卡软化点 | ASTM D-1525 | 42.2 | ℃ | |
| 维卡软化点 | ISO 306 | 42.2 | ℃ | ||
| 熔融温度 | Internal Method | 77.2 | ℃ |