PPE/PS N300X 沙特基础--产品说明:PPE+PS blend. Unfilled. Non-brominated,non-chlorinated FR system. UL94 V0. High heat. Dielectric strength.Dimensional stability. Suitable for E/E applications.
产品说明:
PPE+PS混合物。未填充。非溴化、非氯化FR系统。UL94 V0。高温。介电强度。尺寸稳定性。适用于E/E应用
PPE/PS N300X物性信息:
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
比重 | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
平衡吸湿 | 0.060 % | 0.060 % | ASTM D570 |
线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
线性成型收缩率,横向 | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
熔体流动速率 | 7.4 g/10 min @Load 5.00 kg, Temperature 280 °C | 7.4 g/10 min @Load 11.0 lb, Temperature 536 °F | ASTM D1238 |
化合物熔体指数 | 7.0 g/10 min @Load 5.00 kg, Temperature 280 °C | 7.0 g/10 min @Load 11.0 lb, Temperature 536 °F | MVR [cm^3/10 min]; ISO 1133 |