Lexan* LUX7630C Polycarbonate (PC) resin is a non-filled resin,suitable for injection molding and extrusion. This non-chlorinated,non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm/ 5VA rating at 3.0mm and is UV stabilized (F1 rating) providingadditional weathering capability. Lexan* LUX7630C is available intransparent natural colors only.
PC LUX7630C物性信息:
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
比重 | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
密度 | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
水分吸收 | 0.110 % | 0.110 % | 23°C / 50% RH; ISO 62 |
饱和吸水率 | 0.14 % | 0.14 % | ISO 62 |
线性成型收缩率,Flow | 0.0055 - 0.0075 cm/cm @Thickness 3.20 mm | 0.0055 - 0.0075 in/in @Thickness 0.126 in | SABIC Method |
线性成型收缩率,横向 | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0060 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
熔体流动速率 | 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C | 5.0 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
化合物熔体指数 | 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C | 5.0 g/10 min @Load 2.65 lb, Temperature 572 °F | MVR [cm^3/10 min]; ISO 1133 |