以下是TRITAN(美国伊士曼)TX1501HF/PCTG共聚聚酯/物性表参数
| Propertya | Test Methodb | Typical Value, Unitsc | |
| General Properties | |||
| Specific Gravity | D 792 | 1.18 | |
| Mold Shrinkage | D 955 | 0.005-0.007 mm/mm (0.005-0.007 in./in.) | |
| Mechanical Properties (ISO Method) | |||
| Tensile Strength @ Yield | ISO 527 | 44 MPa | |
| Tensile Strength @ Break | ISO 527 | 49 MPa | |
| Elongation @ Yield | ISO 527 | 7 % | |
| Elongation @ Break | ISO 527 | 154 % | |
| Tensile Modulus | ISO 527 | 1604 MPa | |
| Flexural Modulus | ISO 178 | 1502 MPa | |
| Flexural Strength | ISO 178 | 60 MPa | |
| Izod Impact Strength, Notched | |||
| @ 23°C | ISO 180 | 83 kJ/m2 | |
| @ -40°C | ISO 180 | 11 kJ/m2 | |
| Mechanical Properties | |||
| Tensile Stress @ Yield | D 638 | 43 MPa (6200 psi) | |
| Tensile Stress @ Break | D 638 | 52 MPa (7500 psi) | |
| Elongation @ Yield | D 638 | 7 % | |
| Elongation @ Break | D 638 | 210 % | |
| Tensile Modulus | D 638 | 1575 MPa (2.28 x 105 psi) | |
| Flexural Modulus | D 790 | 1575 MPa (2.28 x 105 psi) | |
| Flexural Yield Strength | D 790 | 64 MPa (9300 psi) | |
| Rockwell Hardness, R Scale | D 785 | 111 | |
| Izod Impact Strength, Notched | |||
| @ 23°C (73°F) | D 256 | 860 J/m (16.1 ft·lbf/in.) | |
| Impact Strength, Unnotched | |||
| @ 23°C (73°F) | D 4812 | NB | |
| Optical Properties | |||
| Total Transmittance | D 1003 | 91 % | |
| Haze | D 1003 | <1 % | |
| Thermal Properties | |||
| Deflection Temperature | |||
| @ 0.455 MPa (66 psi) | D 648 | 94 °C (201 °F) | |
| @ 1.82 MPa (264 psi) | D 648 | 81 °C (178 °F) | |
| Typical Processing Conditions | |||
| Drying Temperature | 88 °C (190 °F) | ||
| Drying Time | 4-6 hrs | ||
| Processing Melt Temperature | 260-282 °C (500-540 °F) | ||
| Mold Temperature | 38-66 °C (100-150 °F) | ||