阻燃PC 基础创新塑料(美国) D451 40%玻纤增强
产品说明：
LNP THERMOCOMP D451 (or EXTC8141) is a compound based onPolycarbonate resin containing Glass Fiber, Flame Retardant. Addedfeatures of this material include: High modulus, good flatness,good ductility, Non-Brominated & Non-Chlorinated FlameRetardant.
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
|---|---|---|---|---|
| 300°C/2.16kg | ISO1133 | 14.0 | cm3/10min | |
| 300°C/5.0kg | ASTMD1238 | 42.4 | cm3/10min | |
| 熔体质量流动速率 | 300°C/2.16kg | ASTMD1238 | 18 | g/10min |
| 300°C/5.0kg | ASTMD1238 | 57 | g/10min | |
| 收缩率 | MD:24小时 | ASTMD955 | 0.10到0.25 | % |
| TD:24小时 | ASTMD955 | 0.10到0.25 | % | |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 抗张强度2 | 断裂 | ASTMD638 | 143 | Mpa |
| 拉伸模量1 | ASTMD638 | 11700 | Mpa | |
| 伸长率3 | 断裂 | ASTMD638 | 2.3 | % |
| 弯曲模量4 | 50.0mm跨距 | ASTMD790 | 9750 | Mpa |
| 弯曲强度5 | 断裂,50.0mm跨距 | ASTMD790 | 186 | Mpa |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 热变形温度 | 1.8MPa,未退火,3.20mm | ASTMD648 | 114 | °C |
| 线形热膨胀系数 | MD:-40到40°C | ASTME831 | 1.5E-05 | cm/cm/°C |
| TD:-40到40°C | ASTME831 | 5.6E-05 | cm/cm/°C | |
| 冲击性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 简支梁缺口冲击强度6 | 23°C | ISO179/1eA | 13 | kJ/m² |
| 简支梁无缺口冲击强度7 | 23°C | ISO179/1eU | 33 | kJ/m² |
| 悬臂梁无缺口冲击强度 | 23°C | ASTMD4812 | 520 | J/m |
| 可燃性 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| UL阻燃等级 | 0.800mm | UL94 | V-0 |
阻燃PC 基础创新塑料(美国)D451是一种无溴、有延展性的塑料，被广泛应用于电子电器领域，尤其是电子显示器领域。这种塑料具有非常好的阻燃性能，能够保护设备免受火灾的威胁。同时，40%玻纤增强的添加使得这种塑料在强度和刚度方面表现更加优异，能够承受较大的冲击载荷和振动。此外，这种塑料还具有良好的耐热性和耐化学品性能，能够在恶劣的环境下长期稳定运行。
阻燃PC 基础创新塑料(美国)D451是一种绿色环保的材料，不含有害物质，符合环保要求。此外，它的价格也非常具有竞争力，仅为25元/千克，非常适合规模生产。因此，在电子电器领域，这种塑料已经成为了非常流行的选择。