PA66美国首诺 R543H 润滑

Vydyne® R543H

Polyamide 66

Ascend Performance Materials Operations LLC

43% 玻璃纤维增强材料

产品说明：

Vydyne R543H is general-purpose, 43% glass-fiber reinforced PA66resin. Available in natural, it is an injection-molding grade resinthat is lubricated for machine feed, flow and mold release.

Glass-reinforced Vydyne resins provide a higher heat distortiontemperature, better resistance to creep, higher impact and betterdimensional stability when compared with unreinforced PA66. Theseproducts have good chemical resistance to a broad range ofchemicals, including many aliphatic and aromatic hydrocarbons foundin most solvents, gasoline, hydraulic fluids, greases and machineoils.

Vydyne R543H resin has tensile strength and modulus properties justbelow aluminum and zinc and can replace these metals in numerousapplications due to an excellent balance of properties. Reductionin production costs, energy consumption and part weight are keyadvantages of Vydyne glass-reinforced PA66 resins over aluminumand/ or zinc die-cast parts.

Vydyne R543H is formulated to minimize the oxidative and thermaldegradation of the PA66 polymer when exposed to elevatedtemperatures for extended periods of time. Vydyne R543H providesimproved retention of physical properties under exposure tolong-term heat. The continuous operating use temperature is 275° F,with short-term peak temperatures as high as 475° F.

Typical Applications/End Uses:
To come

物性信息：

基本信息
黄卡编号

E70062-249089

填料/增强材料

玻璃纤维增强材料, 43% 填料按重量

添加剂

热稳定剂

润滑剂

特性

尺寸稳定性良好

刚性，高

高拉伸强度

高强度

抗溶剂性

抗撞击性，良好

良好的抗蠕变性

良好的流动性

耐化学性良好

耐汽油性

耐油性能

耐油脂性能

热稳定性

润滑

脱模性能良好

用途

草坪和园林设备

齿轮

动力/其它工具

汽车的发动机罩下的零件

外壳

机构评级

ASTM D 4066 PA012G45

ASTM D 6779 PA012G45

UL文件号

E70062

外观

自然色

形式

粒子

加工方法

注射成型

多点数据

Isothermal Stress vs. Strain (ISO 11403-1)

物理性能干燥调节后的单位制测试方法密度1.50--g/cm³ISO 1183收缩率


ISO 294-4     垂直流动方向: 23°C, 2.00 mm0.90--%ISO294-4     流动方向 :23°C, 2.00 mm0.40--%ISO 294-4吸水率


ISO 62     23°C, 24hr0.60--%ISO 62     平衡, 23°C, 50% RH1.5--%ISO62机械性能干燥调节后的单位制测试方法拉伸模量 (23°C)1480011300MPaISO 527-2拉伸应力 (断裂, 23°C)225170MPaISO 527-2拉伸应变 (断裂, 23°C)3.04.0%ISO 527-2弯曲模量 (23°C)125009400MPaISO 178弯曲应力 (23°C)340250MPaISO 178泊松比0.40--
ISO 527-2冲击性能干燥调节后的单位制测试方法简支梁缺口冲击强度


ISO 179     -30°C1314kJ/m²ISO179     23°C1420kJ/m²ISO 179简支梁无缺口冲击强度


ISO 179     -30°C8790kJ/m²ISO179     23°C9295kJ/m²ISO 179悬壁梁缺口冲击强度


ISO 180     -30°C1313kJ/m²ISO180     23°C1319kJ/m²ISO 180热性能干燥调节后的单位制测试方法热变形温度



     0.45 MPa,未退火260--°CISO75-2/B     1.8 MPa,未退火252--°CISO 75-2/A熔融温度260--°CISO 11357-3线形热膨胀系数


ISO 11359-2     流动 :23 到 55°C, 2.00 mm1.6E-5--cm/cm/°CISO11359-2     横向 : 23到 55°C, 2.00 mm1.0E-4--cm/cm/°CISO 11359-2RTI Elec


UL 746     0.750mm140--°CUL 746     1.50 mm140--°CUL746     3.00mm140--°CUL 746RTI Imp


UL 746     0.750mm130--°CUL 746     1.50 mm130--°CUL746     3.00mm130--°CUL 746RTI


UL 746     0.750mm140--°CUL 746     1.50 mm140--°CUL746     3.00mm140--°CUL 746电气性能干燥调节后的单位制测试方法体积电阻率 (0.750 mm)1.0E+12--ohms·cmIEC60093介电强度 (1.00 mm)20--kV/mmIEC60243耐电弧性 (3.00 mm)PLC 5--
ASTM D495漏电起痕指数 (3.00 mm)400 到599--VIEC 60112高电弧燃烧指数(HAI)


UL 746     0.750mmPLC 0--
UL 746     1.50mmPLC 0--
UL 746     3.00mmPLC 0--
UL 746高电压电弧起痕速率 (HVTR)PLC 1--
UL 746热丝引燃 (HWI)


UL 746     0.750mmPLC 4--
UL 746     1.50mmPLC 3--
UL 746     3.00mmPLC 4--
UL 746可燃性干燥调节后的单位制测试方法UL 阻燃等级


UL 94     0.750mmHB--
UL 94     1.50mmHB--
UL 94     3.00mmHB--
UL 94灼热丝易燃指数


IEC 60695-2-12     0.750 mm675--°CIEC60695-2-12     1.50mm675--°CIEC60695-2-12     3.00mm960--°CIEC 60695-2-12热灯丝点火温度


IEC 60695-2-13     0.750 mm700--°CIEC60695-2-13     1.50mm700--°CIEC60695-2-13     3.00mm750--°CIEC 60695-2-13极限氧指数25--%ISO 4589-2补充信息干燥调节后的
测试方法Automotive Materials - (thickness d = 1mm)+--
FMVSS 302注射干燥单位制
干燥温度80.0°C
干燥时间4.0hr
建议的*大回制料比例25%
料筒后部温度280 到 310°C
料筒中部温度280 到 310°C
料筒前部温度280 到 310°C
射嘴温度280 到 310°C
加工（熔体）温度285 到 305°C
模具温度65.0 到 95.0°C

PA66美国首诺 R543H 润滑

PA66美国首诺 R543H 润滑

PA66美国首诺 R543H 润滑

PA66 美国首诺R543H尼龙树脂是一种非常典型的工程塑料，具有异常坚固、耐热以及耐热的特性。除了用于汽车部件、连接器以及其他电子和机械部件之外，

PA66 美国首诺 R543H工程塑胶特性 1. 强韧性佳、耐衝击性优良。 2. 耐磨耗性佳、具自润滑性。 3.耐热性良好、阻燃性较好、具自熄性。 4. 气体阻隔性、耐药品行优异。 5.强度、精度、抗热变形、阻燃要求的产品适用。

电气、 电子类 ：家电外壳、电器接头套、吹风 机集风口、断电器、农机工具 外壳、电热器外壳、风扇外壳、继电器外壳等。 

汽车 工业类 汽车把手、门把、脚踏车刹车 把手、脚踏车轮框、踏板护套。 

其他 工业类 齿轮、风扇叶片、捲线轴、各 式扣具、马达外壳。 

其他类 网拍颈箍、迴力球拍框、溜冰 鞋底座、连接器、行李箱轮子。

PA66 美国首诺 R543H成形时的模具温度和干燥条件

我公司的高性能聚酰胺树脂PA66的射出成形，适合选定比较高的模具温度（模具表面温度120～140℃），这样如果在80℃左右的模温成形之后，需要进行退火处理（130℃下1小时左右），以提高成形品的结晶化度，从而确保强度和刚性。在吸湿的状态下，可能在成形品的表面会产生银条（银色）等异常，建议在成形前进行热风干燥（在80℃下12小时以上或120℃下4小时以上）

PA66 美国首诺 R543H特点：

在较大温度范围内具有高强度高模数的优越性

成型尺寸稳定性高于聚酰胺，低吸水率使其具有高强度的优越性

热膨胀系数低，与合金相当

对油类和有机溶剂有较高抵抗性