Specific Gravity比重

1.39 g/cc

1.39 g/cc

DAM; ASTM D792

Density密度

1.39 g/cc

0.0502 lb/in³

DAM; ISO 1183

Filler Content填料含量

33 %

33 %

DAM

Linear Mold Shrinkage线性收缩率

0.0020 cm/cm
@Thickness 1.60 mm

0.0020 in/in
@Thickness 0.0630 in

Flow; DAM

Linear Mold Shrinkage, Flow线性收缩率/流动

0.0030 cm/cm
@Thickness 2.00 mm

0.0030 in/in
@Thickness 0.0787 in

Parallel; DAM; ISO 294-4

Linear Mold Shrinkage, Transverse线性收缩率/横向

0.011 cm/cm
@Thickness 2.00 mm

0.011 in/in
@Thickness 0.0787 in

Normal; DAM; ISO 294-4

Mechanical Properties力学性能

Tensile Strength at Break断裂拉伸强度

140 MPa
@Temperature 23.0 °C

20300 psi
@Temperature 73.4 °F

50%RH; ISO 527

200 MPa
@Temperature 23.0 °C

29000 psi
@Temperature 73.4 °F

DAM; ISO 527

Tensile Strength拉伸强度

186 MPa
@Temperature 23.0 °C

27000 psi
@Temperature 73.4 °F

DAM; ASTM D638

Tensile Stress拉伸应力

0.000 MPa
@Strain 0.000 %,
Temperature -40.0 °C

0.000 psi
@Strain 0.000 %,
Temperature -40.0 °F

DAM; ISO 11403-1/-2

29.93 MPa
@Strain 0.500 %,
Temperature 80.0 °C

4341 psi
@Strain 0.500 %,
Temperature 176 °F

49.8 MPa
@Strain 0.500 %,
Temperature 23.0 °C

7220 psi
@Strain 0.500 %,
Temperature 73.4 °F

59.965 MPa
@Strain 1.20 %,
Temperature 60.0 °C

8697.2 psi
@Strain 1.20 %,
Temperature 140 °F

50%RH; ISO 11403-1/-2

79.94 MPa
@Strain 3.60 %,
Temperature 120 °C

11590 psi
@Strain 3.60 %,
Temperature 248 °F

99.83 MPa
@Strain 1.10 %,
Temperature 23.0 °C

14480 psi
@Strain 1.10 %,
Temperature 73.4 °F