| 日本出光 PC IV2700规格用途 |
| 其它 其它 其它 | ||
| 日本出光 聚碳酸酯 IV2700技术参数 |
| 性能项目 | 试验条件 | 测试方法 | 测试数据 | |
| 比重 | ASTM D-792 | 1.2 | ||
| 熔融指数 | 300℃ 1.2kg | ISO 1133(ASTM D-1238) | 5 | g/10分 |
| 吸水率 | 23℃水中24h | ASTM D-570 | 0.23 | % |
| 引张弹性率 | ISO R-527(ASTM D-638) | 2300(23500) | MPa(Kg/cm | |
| 挠曲弹性率 | ISO 178(ASTM D-790) | 2350(24000) | MPa(Kg/cm | |
| 引张破坏伸率 | ISO R 527(ASTM D-638) | 130 | % | |
| 引张降伏强度 | ISO R 527(ASTM D-638) | 64(650) | MPa(Kg/cm | |
| 挠曲强度 | ISO 178(ASTM D-790) | 95(970) | MPa(Kg/cm | |
| IZOD冲击强度 | 4mm with notch 3.2mm with notch | ISO 180（ASTM D-256） | 80(100) | KJ/m |
| 引张破坏强度 | ISO R 527(ASTM D-638) | 78(800) | MPa(Kg/cm | |
| 洛氏硬度 | ISO 2039-2（ASTM D-785） | R120(M75) | ||
| 诱电正接 | 60Hz(10 | ASTM D-150 | 6.6×10 | |
| 绝缘破坏电压 | 1.6mm厚 | ASTM D-149 | 30 | Kv/mm |
| 耐电弧性 | ASTM D-495 | 110 | Sec | |
| 体积固有抵抗 | ASTM D-257 | 10 | Ωcm | |
| 诱电率 | 60Hz(10 | ASTM D-150 | 2.91(2.85) | |
| 线膨胀系数 | ASTM D 696(ASTM D-695) | 6.5 | ×10 | |
| 光线透过率 | 3mm厚 | ASTM D-1003 | 85-89 | % |
| 维卡软化点 | ISO 306 | 150 | ℃ | |
| 热变形温度 | 1.8Mpa 18.6kg/cm | ISO 75（ASTM D-648） | 135 | ℃ |
| 燃烧性 | 1.47mm厚 | UL 94 | V-2 | |
| 泰伯磨耗量 | 1,000round | ASTM D-1044 | 12 | mg |
| 成形收缩率 | ASTM D-955 | 0.5-0.7 | % | |