PTFE 日本大金 MG-1050F 耐磨性耐高温挤出级
产品说明：
25% glass fiber filled. Highapparent density and free-flowing properties. High wear resistance,low friction, good electrical properties.
Applications: Mechanical andelectrical service. Available in all forms (e.g. bearings, gaskets,valve seats, packings.
Information provided by DaikinIndustries.
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 2.13 - 2.22 g/cc | 2.13 - 2.22 g/cc | ASTM D792 |
| 吸水率 | 0.00 % @Thickness 8.50 mm, Time 86400sec | 0.00 % @Thickness 0.335 in, Time 24.0hour | ASTM D570 |
| 粘度 | 1.00e+13 - 1.00e+15 cP @Temperature 340 - 380°C | 1.00e+13 - 1.00e+15 cP @Temperature 644 - 716°F | Melt viscosity |
| 线性成型收缩率 | 0.020 - 0.050 cm/cm | 0.020 - 0.050 in/in | |
| 变形 | 5.0 % | 5.0 % | 6.7 MPa load, at 100°C, 24 hrs; ASTMD621 |
| 7.0 % | 7.0 % | 13.7 MPa load, at 25°C, 24 hrs; ASTMD621 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 50 - 65 | 50 - 65 | |
| 抗张强度(断裂) | 20.0 - 45.0 MPa | 2900 - 6530 psi | ASTM D638 |
| 伸长率 (断裂) | 200 - 450 % | 200 - 450 % | ASTM D638 |
| 拉伸模量 | 0.392 GPa | 56.9 ksi | ASTM D638 |
| 弯曲模量 | 0.490 - 0.588 GPa | 71.1 - 85.3 ksi | ASTM D790 |
| 抗压强度 | 5.00 - 6.00 MPa @Temperature 25.0 °C | 725 - 870 psi @Temperature 77.0 °F | 1% deformation; ASTMD695 |
| 悬壁梁无缺口冲击强度 | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| 摩擦系数 | 0.15 - 0.30 | 0.15 - 0.30 | Non-lubricating |
| 静态摩擦系数 | 0.020 | 0.020 | Coated-steel surface |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | <= 1.00e+18 ohm-cm | <= 1.00e+18 ohm-cm | ASTM D257 |
| 介电常数 | 2.1 @Frequency 1000 Hz | 2.1 @Frequency 1000 Hz | ASTM D150 |
| 2.1 @Frequency 1e+6 Hz | 2.1 @Frequency 1e+6 Hz | ASTM D150 | |
| 介电强度 | 19.0 kV/mm @Thickness 3.20 mm | 483 kV/in @Thickness 0.126 in | Short time; ASTM D149 |
| 耗散因数 | <= 0.000010 @Frequency 1000 Hz | <= 0.000010 @Frequency 1000 Hz | ASTM D150 |
| 0.000020 @Frequency 1e+6 Hz | 0.000020 @Frequency 1e+6 Hz | ASTM D150 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | 100 µm/m-°C @Temperature 23.0 - 60.0°C | 55.6 µin/in-°F @Temperature 73.4 - 140°F | ASTM D696 |
| 导热系数 | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | ASTM C177 |
| 熔融温度 | 327 °C | 621 °F | |
| *高工作温度, Air | 260 °C | 500 °F | Continuous use |
| 可燃性(UL94) | V-0 | V-0 | |
| 极限氧指数 | >= 95 % | >= 95 % | ASTM D2863 |
| 材料描述 | 测试方法 | |
|---|---|---|
| 耐化学性 | Excellent | |
| Contact Angle | 110 | Angle to level |
| Weatherability | Excellent |
PTFE 日本大金 MG-1050F 耐磨性耐高温挤出级
供应
PTFE上海大金氟涂料EK-3705S-201L
PTFE上海大金氟涂料EK-3709S-201L
PTFE日本大金F-104115000
PTFE日本大金F-201120000
PTFE日本大金FA-500148000
PTFE日本大金F-L2120000
PTFE日本大金L-5(粉)80000
PTFE日本大金L-5F120000
PTFE日本大金LB-202150000
PTFE日本大金M111(微粉)
PTFE日本大金M112(微粉)
PTFE日本大金M-18118000
PTFE日本大金M-18F100000
PTFE日本大金M-2001120000
PTFE日本大金M-221118000
PTFE日本大金M531140000
PTFE日本大金M532150000
PTFE日本大金M533150000
PTFE日本大金MG-1030F
PTFE日本大金MG-1050F
PTFE日本大金超细粉
PTFE美国3M2072Z215000
PTFE美国3MTF1645125000
PTFE美国3MTF1750125000
PTFE美国3MTFM1700128000
PTFE美国苏威F-284
PTFE美国科慕421G-119
PTFE美国科慕6000X
PTFE美国科慕601X
PTFE美国科慕62X
PTFE美国科慕65AX
PTFE美国科慕6CX
PTFE美国科慕7X
PTFE美国科慕D30LX
3月17日星期五，我们收到信息，一些材料的进口关税将会提高