Polycarbonate
SABIC Innovative Plastics
10% 玻璃纤维增强材料
产品说明：
10% GR PC. Optimum combination of high modulus plus excellentimpact strength and flame retardance. Internal mold release.
物性信息：
基本信息黄卡编号
E121562-220886
填料/增强材料玻璃纤维增强材料, 10% 填料按重量
添加剂脱模
特性刚性，高
抗撞击性，良好
阻燃性
加工方法注射成型
多点数据Coefficient of Thermal Expansion vs. Temperature (ASTM E831)
Flexural DMA (ASTM D4065)
Pressure-Volume-Temperature (PVT - Zoller Method)
Shear DMA (ASTM D4065)
Specific Heat vs. Temperature (ASTM D3417)
Tensile Fatigue
Tensile Stress vs. Strain (ASTM D638)
Thermal Conductivity vs. Temperature (ASTM E1530)
Viscosity vs. Shear Rate (ASTM D3835)
物理性能额定值单位制测试方法比重ASTM D792 --1.27g/cm³ASTMD792 --1.25g/cm³ASTM D792特定体积0.802cm³/gASTMD792可燃性额定值单位制测试方法Radiant Panel Listing (UL)YES
物理性能额定值单位制测试方法熔流率（熔体流动速率） (300°C/1.2kg)7.5g/10 minASTM D1238收缩率 - 流动 (3.20 mm)0.20 到 0.40%内部方法吸水率
ASTM D570 24hr0.12%ASTM D570 平衡, 23°C0.31%ASTM D570室外适用性f2
UL 746C硬度额定值单位制测试方法洛氏硬度
ASTM D785 M级85
ASTM D785 R级124
ASTM D785机械性能额定值单位制测试方法抗张强度 1
ASTM D638 屈服66.2MPaASTMD638 断裂55.2MPaASTM D638伸长率 2
ASTM D638 屈服8.0%ASTMD638 断裂15%ASTMD638弯曲模量 3(50.0 mm跨距)3450MPaASTM D790弯曲强度 4(屈服, 50.0 mm 跨距)103MPaASTMD790泰伯耐磨性 (1000 Cycles, 1000 g, CS-17转轮)11.0mgASTM D1044冲击性能额定值单位制测试方法悬壁梁缺口冲击强度 (23°C)110J/mASTM D256无缺口悬臂梁冲击 (23°C)2100J/mASTM D4812落锤冲击 (23°C)102JASTMD3029拉伸冲击强度 5158kJ/m²ASTMD1822热性能额定值单位制测试方法载荷下热变形温度
ASTM D648 0.45 MPa,未退火, 6.40 mm146°CASTMD648 1.8 MPa, 未退火,6.40 mm142°CASTM D648维卡软化温度154°CASTMD1525 6线形热膨胀系数 - 流动 (-40 到 95°C)3.2E-5cm/cm/°CASTME831比热1210J/kg/°CASTM C351导热系数0.20W/m/KASTM C177RTI Elec130°CUL746RTI Imp130°CUL 746RTI130°CUL 746电气性能额定值单位制测试方法体积电阻率>1.0E+17ohms·cmASTM D257介电强度 (3.20 mm, inAir)18kV/mmASTM D149介电常数
ASTM D150 50Hz3.10
ASTM D150 60Hz3.10
ASTM D150 1MHz3.05
ASTM D150耗散因数
ASTM D150 50Hz8.0E-4
ASTM D150 60Hz8.0E-4
ASTM D150 1MHz7.5E-3
ASTM D150耐电弧性 7PLC 7
ASTM D495相比耐漏电起痕指数(CTI)PLC 3
UL 746高电弧燃烧指数(HAI)PLC 4
UL 746高电压电弧起痕速率 (HVTR)PLC 4
UL 746热丝引燃 (HWI)PLC 1
UL 746可燃性额定值单位制测试方法UL 阻燃等级
UL 94 1.52mmV-0
UL 94 3.05mm5VA
UL 94极限氧指数36%ASTM D2863