ABS 台湾奇美 PA-757GJ01-物性参数
| 性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 | |
| 机械性能 | 拉伸强度(引张强度) | ASTM D638/ISO 527 | kg/cm²(MPa)[Lb/in2] | ||
| 断裂伸长率 | ASTM D638/ISO 527 | % | |||
| 拉伸模量 | ASTM D638/ISO 527 | kg/cm²(MPa)[Lb/in2] | |||
| 拉伸屈服伸长率(延伸率) | ASTM D638/ISO 527 | % | |||
| 拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | % | |||
| 弯曲模量(弯曲弹性率) | ASTM D790/ISO 178 | kg/cm²(MPa)[Lb/in2] | |||
| 弯曲强度 | ASTM D790/ISO 178 | kg/cm²(MPa)[Lb/in2] | |||
| 洛氏硬度 | ASTM D785 | 115 | |||
| IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 | kg・cm/cm(J/M)ft・lb/in | ||
| 1/4" -30℃ | ASTM D256/ISO 179 | kg・cm/cm(J/M)ft・lb/in | |||
| 1/8" 23℃ | ASTM D256/ISO 179 | kg・cm/cm(J/M)ft・lb/in | |||
| 1/8" -30℃ | ASTM D256/ISO 179 | kg・cm/cm(J/M)ft・lb/in | |||
| Charpy冲击强度 | 23℃ （缺口） | ASTM D256/ISO 179 | kg・cm/cm(J/M)ft・lb/in | ||
| -30℃（缺口） | ASTM D256/ISO 179 | kg・cm/cm(J/M)ft・lb/in | |||
| 23℃（无缺口） | ASTM D256/ISO 179 | kg・cm/cm(J/M)ft・lb/in | |||
| -30℃（无缺口） | ASTM D256/ISO 179 | kg・cm/cm(J/M)ft・lb/in | |||
| 物性性能 | 比重（密度） | ASTM D792/ISO 1183 | 1.04 | ||
| 成型收缩率 | ASTM D955 | % | |||
| 熔融指数（流动系数） | 200℃/5kg | ASTM D1238/ISO 1133 | 1.7 | g/10min | |
| 220℃/10kg | ASTM D1238/ISO 1133 | g/10min | |||
| 吸水率 23℃/24H | ASTM D570/ISO 62 | % | |||
| 热性能 | 热变形温度 | 退火 | ASTM D648/ISO 75 | 208 | ℃（�H） |
| 未退火 | ASTM D648/ISO 75 | 189 | ℃（�H） | ||
| 维卡软化点 | ASTM D1525/ISO R306 | 217 | ℃（�H） | ||
| 熔点 | - | ℃（�H） | |||
| 燃烧性（率） | UL94 | ||||
| 线性膨胀系数 | ASTM D696/ISO 11359 | mm/mm.℃ | |||
| 加工条件 | 干燥条件 | ||||
| 加工温度 | 射嘴 | ℃ | |||
| 料筒前段 | ℃ | ||||
| 料筒中段 | ℃ | ||||
| 料筒后段 | ℃ | ||||
| 熔体温度 | ℃ | ||||
| 模具温度 | ℃ | ||||
| 压力 | 注塑压力 | Mpa | |||
| 保压压力 | Mpa | ||||
| 背压 | Mpa | ||||
| 螺杆转速 | rpm | ||||