Polyphenylene Ether + PS
SABIC Innovative Plastics
20% 玻璃纤维增强材料
产品说明:
PPE+PS blend. 20% Glass reinforced. UL746C F1. NSF 61 listing inseveral colors (restrictions apply). FDA compliance (restrictionsapply). Low water absorption. Hydrolytic stability. Dimensionalstability. Suitable for fluid engineering applications includingpump housings and impellers, valve components and others.
物性信息:
基本信息黄卡编号
E121562-221161
填料/增强材料玻璃纤维增强材料, 20% 填料按重量
特性尺寸稳定性良好
水解稳定
吸水低或不吸水
机构评级FDA 未评级
NSF 61
加工方法注射成型
多点数据Coefficient of Thermal Expansion vs. Temperature (ASTM E831)
Elastic Modulus vs Temperature (ASTM D4065)
Flexural DMA (ASTM D4065)
Instrumented Impact (Energy) (ASTM D3763)
Instrumented Impact (Load) (ASTM D3763)
Pressure-Volume-Temperature (PVT - Zoller Method)
Shear DMA (ASTM D4065)
Specific Heat vs. Temperature (ASTM D3417)
Tensile Creep (ASTM D2990)
Tensile Fatigue
Tensile Stress vs. Strain (ASTM D638)
Thermal Conductivity vs. Temperature (ASTM E1530)
Viscosity vs. Shear Rate (ASTM D3835)
物理性能额定值单位制测试方法比重1.20g/cm³ASTM D792熔流率(熔体流动速率) (300°C/5.0 kg)9.0g/10 minASTMD1238溶化体积流率(MVR) (300°C/5.0kg)8.10cm³/10minISO 1133收缩率 - 流动 (3.20 mm)0.20 到 0.50%内部方法吸水率 (24 hr)0.060%ASTM D570室外适用性f1UL 746C硬度额定值单位制测试方法洛氏硬度 (L计秤)106
ASTM D785机械性能额定值单位制测试方法拉伸模量
-- 16200MPaASTMD638 --7070MPaISO 527-2/1抗张强度
断裂 290.0MPaASTMD638 断裂97.3MPaISO 527-2/5伸长率
断裂 32.6%ASTMD638 断裂2.5%ISO527-2/5弯曲模量
50.0 mm跨距 45800MPaASTMD790 -- 56540MPaISO 178弯曲应力
--167MPaISO178 屈服, 50.0 mm跨距 6160MPaASTMD790冲击性能额定值单位制测试方法简支梁缺口冲击强度 (23°C)12kJ/m²ISO 179/2C悬壁梁缺口冲击强度
-40°C96J/mASTMD256 23°C120J/mASTMD256 23°C 711kJ/m²ISO180/1A无缺口悬臂梁冲击 (23°C)650J/mASTMD4812装有测量仪表的落镖冲击 (23°C, TotalEnergy)22.6JASTM D3763热性能额定值单位制测试方法载荷下热变形温度
0.45 MPa, 未退火, 3.20mm141°CASTM D648 0.45 MPa, 未退火, 6.40 mm143°CASTMD648 0.45 MPa, 未退火,100 mm 跨距 8143°CISO75-2/Be 1.8 MPa, 未退火,3.20 mm135°CASTM D648 1.8 MPa, 未退火, 6.40 mm138°CASTMD648 1.8 MPa, 未退火, 100mm 跨距 9137°CISO 75-2/Ae维卡软化温度
--143°CISO306/B50 --146°CISO 306/B120线形热膨胀系数
ASTM E831 流动 : -40 到40°C2.9E-5cm/cm/°CASTME831 横向 : -40 到40°C8.3E-5cm/cm/°CASTM E831RTI Elec90.0°CUL 746RTIImp90.0°CUL 746RTI90.0°CUL 746电气性能额定值单位制测试方法介电强度 (3.20 mm, in Oil)17kV/mmASTM D149介电常数
ASTM D150 50Hz2.86
ASTM D150 60Hz2.86
ASTM D150耗散因数
ASTM D150 50Hz8.0E-4
ASTM D150 60Hz8.0E-4
ASTM D150耐电弧性 10PLC 7
ASTM D495高电弧燃烧指数(HAI)PLC 4
UL 746高电压电弧起痕速率 (HVTR)PLC 4
UL 746热丝引燃 (HWI)PLC 4
UL 746可燃性额定值单位制测试方法UL 阻燃等级 (1.47mm)HB
UL 94极限氧指数26%ASTM D2863注射额定值单位制
干燥温度110 到 121°C
干燥时间3.0 到 4.0hr
干燥时间,大8.0hr
建议的大水分含量0.020%
建议注射量30 到 70%
料筒后部温度266 到 316°C
料筒中部温度277 到 321°C
料筒前部温度288 到 327°C
射嘴温度299 到 327°C
加工(熔体)温度299 到 327°C
模具温度82.2 到 110°C
背压0.345 到 0.689MPa
螺杆转速20 到 100rpm
备注1 .5.0 mm/min2 .类型 1, 5.0 mm/min3 .类型 1, 5.0 mm/min4 .1.3 mm/min5.2.0 mm/min6 .1.3 mm/min7 .80*10*48 .120*10*4 mm9 .120*10*4 mm10.钨电极
基础创新PPO GFN2 加纤20
基础创新PPO GFN2 加纤20