产品参数
Teflon®PTFE 8A
聚四氟乙烯
TheChemours Company
产品说明:
Teflon ® PTFE 8A X is a free-flowing white powder composed ofrelatively large particles. It has high bulk density and goodpowder flow. It's most unique features are improved moldability atlower pressure and improved surface smoothness of finished parts.The high bulk density and low compression ratio of Teflon® PTFE 8AX permit the use of shallow molds for small parts and complexshapes. Good powder flow is necessary for use in e thatfeeds resin automatically, and for filling deep and narrow moldsthat are pressed isostatically. Reduced pressure is an advantagefor moldings with large surface area and for isostatic molding.Teflon ® PTFE 8A X is often preferred for molding thick sheets andfor isostatic moldings. It is sometimes used for ram extrusion ofrod and tubing with thicker cross sections. Properly processedproducts made from neat Teflon ® PTFE 8A X provide the superiorproperties typical of the fluoropolymer resins: retention ofproperties after service at 260 °C (500 °F), useful properties at-240 °C (-400 °F), chemical inertness to nearly all industrialchemicals and solvents, and low friction and antistick surfaces.Dielectric properties are outstanding and stable with frequency andtemperature. Molded products have moderate stiffness and highultimate elongation. In a flame situation, products of Teflon ®PTFE 8A X resist ignition and do not themselves promote flamespread. When ignited by flame from other sources, theircontribution of heat is small and with very little smoke.Statements, or data, regarding behavior in a flame situation arenot intended to reflect hazards presented by this or any othermaterial when under actual fire conditions.
Typical Applications
Many end products are fabricated from moldings of Teflon ® PTFE 8AX, including small parts such as ball valve seats, seals, discs,and lab ware. Thick molded sheets are stock shapes made from Teflon® PTFE 8A X. It is also chosen for lining pipes, valves, and valveplugs—and for ducting, expansion bellows, piston rings, and otherlarge complex moldings.
总览 | |
材料状态 |
|
资料 1 |
|
搜索 UL 黄卡 |
|
供货地区 | 北美洲拉丁美洲欧洲亚太地区 |
特性 | 低摩擦系数低烟度抗溶剂性良好的成型性能良好的电气性能良好的流动性良好刚性耐化学品性能,良好食品接触的合规性延高的拉伸率优良外观 |
用途 | 衬里阀门/阀门部件密封件片材实验室器具 |
机构评级 | FDA 21CFR 177.1550欧洲 No 10/2011 |
外观 |
|
形式 |
|
加工方法 | 烧结柱塞压出 |
物理性能 | 额定值 | 单位制 | 测试方法 |
密度 / 比重 | 2.14 | g/cm³ | ASTMD4894 |
表观密度 | 0.68 | ASTMD4894 | |
收缩率 - 流动 2 | 2.8 | % | ASTMD4894 |
平均颗粒尺寸 | 490 | µm | ASTMD4894 |
机械性能 | 额定值 | ||
抗张强度 | 41.4 | MPa | ASTMD4894 |
伸长率 (断裂) | 330 | ASTMD4894 |
热性能 | 额定值 | ||
熔融峰值温度 | ASTMD4894 | ||
-- 3 | 317 到 337 | °C | |
-- 4 | 332 到 352 |
补充信息 | 额定值 | ||
Flowability 5 | 221 | g/min |