物理性能测试条件测试方法测试结果单位收缩率MD:1.00mm3%0.80到1.5--MD:3.00mm4%1.5到2.2--泰伯磨耗量1000g,CS-17ASTMD-10443.5%水|-mg/1000次1000g,CS-17ASTMD-1044无水|8mg/1000次吸水率23°C,24hr%1.2--饱和,23°C%8.0--机械性能测试条件测试方法测试结果单位断裂伸长率23℃ASTMD-638无水|90%23℃ASTM D-6383.5%水|<200%剪切强度23°CMPa80.075.0抗剪强度23℃ASTM D-7323.5%水|770kg/cm223℃ASTMD-732无水|790kg/cm2抗拉屈服强度23℃ASTM D-6383.5%水|530kg/cm280℃ASTMD-638无水|430kg/cm280℃ASTM D-6383.5%水|400kg/cm223℃ASTMD-638无水|800kg/cm2-40℃ASTM D-638无水|1150kg/cm2-40℃ASTMD-6383.5%水|1100kg/cm2拉伸应变屈服,23°C%1.5--断裂,23°C%2550拉伸应力-40°CMPa11523°CMPa80.050.080°CMPa40.040.0洛氏硬度23℃ASTM D-785无水|97M-标度23℃ASTMD-7853.5%水|-M-标度23℃ASTM D-785无水|119R-标度23℃ASTMD-7853.5%水|100R-标度摩擦系数-vs.Metal5
0.15到0.20--挠曲模量23℃ASTM D-790无水|29000kg/cm280℃ASTMD-790无水|9000kg/cm280℃ASTM D-7903.5%水|5000kg/cm2-40℃ASTMD-790无水|44000kg/cm2-40℃ASTM D-7903.5%水|42000kg/cm223℃ASTMD-7903.5%水|14000kg/cm2挠曲强度23℃ASTM D-790无水|1150kg/cm223℃ASTMD-7903.5%水|650kg/cm2-40℃ASTM D-7903.5%水|1300kg/cm280℃ASTMD-790无水|640kg/cm280℃ASTM D-7903.5%水|400kg/cm2-40℃ASTMD-790无水|1450kg/cm2泰伯耐磨性1000Cyclesmg8.00--弯曲模量-40°CMPa4300410023°CMPa2900140080°CMPa900500弯曲强度
ASTM D790/ISO1782.8kg·cm/cm(J/M)ft·lb/in弯曲应力-40°CMPa14012523°CMPa11565.080°CMPa65.040.0压缩强度23℃ASTMD-695无水|910kg/cm223℃ASTMD-6953.5%水|-kg/cm2压缩应力23°CMPa90.0--Charpy冲击强度
ASTM D256/ISO 17950kg·cm/cm(J/M)ft·lb/inIZOD冲击强度-40℃,V缺口1/2ASTMD-256无水|3.5kg·cm/cm-40℃,V缺口1/2ASTMD-2563.5%水|-kg·cm/cm23℃,无缺口1/8
无水|无断裂kg·cm/cm223℃,无缺口1/8
3.5%水|-kg·cm/cm223℃,V缺口1/2ASTM D-256无水|5kg·cm/cm23℃,V缺口1/2ASTMD-2563.5%水|28kg·cm/cm热性能测试条件测试方法测试结果单位UL-94抗燃级1/32"UL 94无水|V-2
1/32"UL 943.5%水|-
比热
无水|0.4Cal/g·℃
3.5%水|-Cal/g·℃
J/kg/°C2100--导热系数
W/m/K0.32--
无水|0.21Kcal/m·hr·℃
3.5%水|-Kcal/m·hr·℃燃烧性(率)
UL94V-2
热变形温度
ASTM D648/ISO75220(0.46MPa)℃(℉)0.45MPa,未退火°C220--热挠曲温度4.6kg/cm2ASTMD-648无水|220℃4.6kg/cm2ASTM D-6483.5%水|-℃熔点
差示扫描测热计DSC无水|265℃
差示扫描测热计DSC3.5%水|-℃熔融温度
°C265--线形热膨胀系数MDcm/cm/°C9.0E-5到1.0E-4--线性膨胀系数
ASTM D696/ISO 113590.32mm/mm.℃线性热膨胀系数
ASTM D-696无水|9-10×10-5cm/cm/℃
ASTM D-6963.5%水|-×10-5cm/cm/℃电气性能测试条件测试方法测试结果单位IEC导电径迹指数
UL 746无水|-V
UL 7463.5%水|530V耗散因数623°C,50Hz
0.060--介电常数50HzASTM D-150无水|1.6
50HzASTM D-1503.5%水|-
ASTM D150/IEC 602503.3
介电常数623°C,50Hz
1.60--损耗因数50HzASTM D-150无水|0.06
50HzASTM D-1503.5%水|-
体积电阻率
ASTM D-2573.5%水|1012-1013Ω.cm
ASTM D-257无水|1014-1015Ω.cm
ohms·cm1.0E+13到1.0E+141.0E+12到1.0E+13相比耐漏电起痕指数CTIV530--冲击性能测试条件测试方法测试结果单位简支梁无缺口冲击强度-40°C
无断裂--23°C
无断裂--硬度测试条件测试方法测试结果单位洛氏硬度R计秤,23°C
119
R计秤,80°C
97--可燃性测试条件测试方法测试结果单位UL阻燃等级0.79mm
V-2--物性性能测试条件测试方法测试结果单位密度
ASTM D792/ISO 11831.14
吸水率 23℃/24H
ASTM D570/ISO 621.2%基本性能测试条件测试方法测试结果单位吸水率23℃,24小时ASTMD-570无水|1.2%23℃,24小时ASTM D-5703.5%水|-%