Westlake Kynar®450
聚偏二氟乙烯
Westlake Plastics Company
产品说明
Manufacturedfrom Kynar® polyvinylidene fluoride resin. This material offersexcellent corrosion and
chemicalresistance at both ambient and elevated temperatures. PVDF is alsoinherently UV stable,
mechanicallytough, abrasion and flame resistant.
ApplicationsInclude:
ChemicalProcess/Storage
Fluidhandling
Semiconductorequipment
Fire-safecomponentry
DIWater Systems
Advantagesof Kynar:
Highpurity
Flameresistant
Easy tomachine
Excellentweatherability
Resinmeets the re of FDA, USDA, USPXX Class VI, 3A, UL, V-0,FM 4910
基本信息
特性
纯度高、抗紫外线性能良好、可切削、良好的抗腐蚀性
良好耐磨损性、耐化学性、良好耐气候影响性能良好、韧性良好
阻燃性
机构评级
FDA未评级FM 4910 UL 2360, Class 1 USDA Unspecified Approval
USP第VI类
外观白色
形式棒材薄膜管道片材
物理性能额定值单位制测试方法
比重 1.78g/cm³ ASTM D792
吸水率 (24hr) 0.030 % ASTM D570
硬度额定值单位制测试方法
肖氏硬度(邵氏 D) 77 ASTM D2240
机械性能额定值单位制测试方法
拉伸模量1720 MPa ASTM D638
抗张强度(屈服) 48.3 MPa ASTM D638
伸长率ASTM D638
屈服 7.0到 13 % ASTM D638
断裂 ASTM D638
弯曲模量2000 MPa ASTM D790
弯曲强度55.2 MPa ASTM D790
冲击性能额定值单位制测试方法
悬壁梁缺口冲击强度160 J/m ASTM D256
无缺口悬臂梁冲击1100 到 4300 J/m ASTM D256
热性能额定值单位制测试方法
载荷下热变形温度ASTM D648
0.45MPa, 未退火 125 到 140 °C ASTM D648
1.8MPa, 未退火 110 °C ASTM D648
连续使用温度138 °C
熔融温度168 °C ASTM D4591
线形热膨胀系数- 流动 1.2E-4 cm/cm/°C ASTM D696
电气性能额定值单位制测试方法
体积电阻率2.0E+14 ohms cm ASTM D257
介电强度(0.127 mm) 63 kV/mm ASTM D149
介电常数 (1kHz) 8.50 ASTM D150
可燃性额定值单位制测试方法
UL 阻燃等级V-0 UL 94
极限氧指数43 % ASTM D2863