Celstran®+PP-GF30-05CN01/10
Polypropylene
Celanese Corporation
30% 长玻璃纤维
产品说明：
Material code according to ISO 1043-1: PP
Polypropylene with 30 weight percent ash content, long
glass fibers reinforced. Impact modified, copolymer. The fibers arechemically coupled to the polypropylene
matrix. The pellets are cylindrical and normally as well as the
embedded fibers 10 mm long.
Parts molded of CELSTRAN have outstanding mechanical propertiessuch
as high strength and stiffness combined with high heatdeflection.
The notched impact strength is increased at elevated and low
temperatures due to the fiber skeleton built in the parts. Thelong
fiber reinforcement reduces creep significantly.
The very isotropic shrinkage in the molded parts minimizes the
warpage.
Complex parts can be manufactured with high reproducibility by
injection molding.
Application field: Functional/structural parts for automotive
物性信息：
| 基本信息 | |
|---|---|
| 填料/增强材料 |
|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 形式 |
|
| 加工方法 |
|
| 树脂ID (ISO 1043) |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.13 | g/cm³ | ISO 1183 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | |||
| -- | 6000 | MPa | ISO 527-2/1A/1 |
| 80°C | 4100 | MPa | ISO 527-2/1A |
| 拉伸应力 | |||
| 断裂 | 95.0 | MPa | ISO 527-2/1A/5 |
| 80°C | 50.0 | MPa | ISO 527-2/1A |
| 拉伸应变 | |||
| 断裂 | 2.4 | % | ISO 527-2/1A/5 |
| 断裂, 80°C | 3.3 | % | ISO 527-2/1A |
| 弯曲模量 | ISO 178 | ||
| 23°C | 6000 | MPa | ISO 178 |
| 80°C | 4000 | MPa | ISO 178 |
| 弯曲应力 | ISO 178 | ||
| 23°C | 150 | MPa | ISO 178 |
| 80°C | 70.0 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179/1eA | ||
| -30°C | 24 | kJ/m² | ISO 179/1eA |
| 23°C | 25 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 | ISO 179/1eU |