Polycarbonate
SABIC Innovative Plastics
产品说明:
LEXAN EXL1330 polycarbonate (PC) siloxane copolymer resin is aUV stabilized opaque injection molding (IM) and sheet extrusiongrade. This resin offers extreme low temperature (-60 C) ductilityin combination with medium flow characteristics and excellentprocessability with opportunities for shorter IM cycle timescompared to standard PC. LEXAN EXL1330 resin is a general purposeproduct available in a wide range of opaque colors and is anexcellent candidate for a broad range of applications.
物性信息:
基本信息添加剂
紫外线稳定剂
特性共聚物
可加工性,良好
快的成型周期
流动性中等
通用
延展性
用途通用
外观不透明
可用颜色
加工方法片材挤出成型
注射成型
多点数据Compressive Stress vs. Strain (ASTM D695)
Flexural DMA (ASTM D4065)
Pressure-Volume-Temperature (PVT - Zoller Method)
Specific Heat vs. Temperature (ASTM D3417)
Tensile Stress vs. Strain (ASTM D638)
Thermal Conductivity vs. Temperature (ASTM E1530)
Viscosity vs. Shear Rate (ASTM D3835)
物理性能额定值单位制测试方法比重1.18g/cm³ASTM D792, ISO1183熔流率(熔体流动速率) (300°C/1.2kg)10g/10 minASTM D1238溶化体积流率(MVR) (300°C/1.2 kg)9.00cm³/10minISO 1133收缩率内部方法 流动 : 3.20mm0.40 到 0.80%内部方法 横向流动 : 3.20 mm0.40 到 0.80%内部方法吸水率
ISO 62 饱和,23°C0.35%ISO 62 平衡, 23°C, 50% RH0.15%ISO62硬度额定值单位制测试方法球压硬度 (H358/30)90.0MPaISO 2039-1机械性能额定值单位制测试方法拉伸模量
-- 12100MPaASTMD638 --2100MPaISO 527-2/1抗张强度
屈服 258.6MPaASTMD638 屈服55.0MPaISO527-2/50 断裂 361.4MPaASTMD638 断裂56.0MPaISO 527-2/50伸长率
屈服 46.0%ASTMD638 屈服5.0%ISO527-2/50 断裂 5130%ASTMD638 断裂>ISO 527-2/50弯曲模量
50.0 mm跨距 62070MPaASTMD790 -- 72100MPaISO 178弯曲应力
--85.0MPaISO178 屈服, 50.0 mm跨距 888.9MPaASTMD790冲击性能额定值单位制测试方法简支梁缺口冲击强度 9
ISO 179/1eA -30°C60kJ/m²ISO179/1eA 23°C75kJ/m²ISO179/1eA简支梁无缺口冲击强度 10
ISO 179/1eU -30°C无断裂
ISO 179/1eU 23°C无断裂
ISO 179/1eU悬壁梁缺口冲击强度
-50°C590J/mASTMD256 -30°C680J/mASTMD256 23°C800J/mASTMD256 23°C, 6.40mm640J/mASTM D256 -30°C 1155kJ/m²ISO180/1A 23°C 1270kJ/m²ISO180/1A无缺口悬臂梁冲击
23°C 131100J/m内部方法 -30°C 14无断裂
ISO 180/1U 23°C 15无断裂
ISO 180/1U装有测量仪表的落镖冲击 (23°C, TotalEnergy)52.9JASTM D3763热性能额定值单位制测试方法载荷下热变形温度
0.45 MPa, 未退火, 3.20mm134°CASTM D648 0.45 MPa, 未退火, 100 mm跨距 16136°CISO75-2/Be 1.8 MPa, 未退火,3.20 mm121°CASTM D648 1.8 MPa, 未退火, 6.40 mm124°CASTMD648 1.8 MPa, 未退火, 100mm 跨距 17125°CISO 75-2/Ae维卡软化温度
--143°CASTMD1525, ISO306/B50 12 18 --145°CISO306/B120Ball Pressure Test (125°C)Pass
IEC 60695-10-2线形热膨胀系数
流动 : -40 到40°C6.7E-5cm/cm/°CASTME831 流动 : 23 到80°C7.2E-5cm/cm/°CISO11359-2 横向 : -40 到40°C6.7E-5cm/cm/°CASTME831 横向 : 23 到80°C7.2E-5cm/cm/°CISO 11359-2RTI Elec125°CUL 746RTIImp115°CUL 746RTI120°CUL 746可燃性额定值单位制测试方法UL 阻燃等级 (0.800 mm)HB
UL 94灼热丝易燃指数
IEC 60695-2-12 0.800mm850°CIEC 60695-2-12 1.00 mm960°CIEC 60695-2-12热灯丝点火温度
IEC 60695-2-13 1.00mm875°CIEC 60695-2-13 3.00 mm875°CIEC 60695-2-13极限氧指数35%ISO4589-2注射额定值单位制
干燥温度121°C
干燥时间3.0 到 4.0hr
干燥时间,*大48hr
建议的*大水分含量0.020%
建议注射量40 到 60%
料筒后部温度217 到 293°C
料筒中部温度282 到 304°C
料筒前部温度293 到 316°C
射嘴温度288 到 310°C
加工(熔体)温度293 到 316°C
模具温度71.0 到 93.0°C
背压0.345 到 0.689MPa
螺杆转速40 到 70rpm
排气孔深度0.025 到 0.076mm
挤出额定值单位制
干燥温度110 到 121°C
干燥时间3.0 到 4.0hr
建议的*大水分含量0.020%
料筒1区温度249 到 288°C
料筒2区温度243 到 271°C
料筒3区温度227 到 254°C
接头温度227 到 254°C
熔体温度243 到 260°C
口模温度238 到 260°C
挤压说明Drying Time (Cumulative): 48 hrsRoll Stack Temp - Bottom: 121 -143 °CRoll Stack Temp - Middle: 82 - 127 °CRoll Stack Temp - Top:77 - 116 °C备注1 .50 mm/min2 .类型 1, 50 mm/min3 .类型 1, 50 mm/min4 .类型1, 50 mm/min5 .类型 1, 50 mm/min6 .1.3 mm/min7 .2.0 mm/min8 .1.3mm/min9 .80*10*3 sp=62mm10 .80*10*3 sp=62mm11 .80*10*312 .80*10*313.Double-Gated14 .80*10*315 .80*10*316 .120*10*4 mm17 .120*10*4 mm18.标准 B (120°C/h), 载荷2 (50N)
PC EXL1330
PC简介
在PC中加入玻纤、碳纤维、硼纤维及石棉纤维等增强材料,可显著提高其疲劳强度、拉伸强度、弹性模量、弯曲强度、压缩强度,显著改善应力开裂性等力学性能及耐热性能,成型收缩率也能进一步下降,但冲击强度有所降低,同时制品将失去透明性。目前增强PC主要用玻纤增强。玻纤含量对增强PC性能的影响:随玻纤含量↑,增强PC的力学性能↑当玻纤含量<10%时,增强效果不显著;当含量>40%时,制品脆性太大,而且熔体流动性差,给成型加工带来一定困难。通常玻纤含量在20~40%的范围内较适宜