泰科纳 PA66 长玻璃纤维PA66-GF50-02 P7 低翘曲性锦纶66塑料胶粒
Celstran®PA66-GF50-02 P7
Polyamide 66
Celanese Corporation
50% 长玻璃纤维
产品说明：
Material code according to ISO 1043-1: PA66
Heat stabilized Nylon 66 reinforced by 50 weight percent longglass
fibers. The pellets are cylindrical and normally as well as the
embedded fibers 7 mm long.
Parts molded of CELSTRAN have outstanding mechanical propertiessuch
as high strength and stiffness combined with high heatdeflection.
The notched impact strength is increased at elevated and low
temperatures due to the fiber skeleton built in the parts. Thelong
fiber reinforcement reduces creep significantly.
The very isotropic shrinkage in the molded parts minimizes the
warpage.
Complex parts can be manufactured with high reproducibility by
injection molding.
Can be used for substituting die cast metal with the advantageof
Weight reduction, no corrosion problems, no post treatment.
物性信息：
| 基本信息 | |
|---|---|
| 填料/增强材料 |
|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 形式 |
|
| 加工方法 |
|
| 树脂ID (ISO 1043) |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.57 | g/cm³ | ISO 1183 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 16600 | MPa | ISO 527-2/1A/1 |
| 拉伸应力 (断裂) | 260 | MPa | ISO 527-2/1A/5 |
| 拉伸应变 (断裂) | 2.1 | % | ISO 527-2/1A/5 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 熔融温度 1 | 260 | °C | ISO 11357-3 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 70.0 到 80.0 | °C | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的*大水分含量 | 0.15 | % | |
| 料斗温度 | 70.0 到 80.0 | °C | |
| 料筒后部温度 | 280 到 285 | °C | |
| 料筒中部温度 | 280 到 290 | °C | |
| 料筒前部温度 | 290 到 300 | °C | |
| 射嘴温度 | 310 到 320 | °C | |
| 加工（熔体）温度 | 310 到 320 | °C | |
| 模具温度 | 90.0 到 120 | °C | |
| 注塑压力 | 120 到 150 | MPa | |
| 注射速度 | 中等 | ||
| 保压 | 50.0 到 80.0 | MPa | |
| 背压 | 0.00 到 3.00 | MPa |