沙伯基础 PBT -- FARADEX WX94736 compound
LNP™FARADEX™ WX94736 compound
Polybutylene Terephthalate
SABIC Innovative Plastics
不锈钢纤维
产品说明：
LNP* FARADEX* WX94736 is a compound based on PBT resincontaining Stainless Steel. Added features of this materialinclude: EMI/RFI Shielding, Electrically Conductive.
Also known as: LNP* FARADEX* Compound PDX-W-94736
Product reorder name: WX94736
物性信息：
| 基本信息 | |
|---|---|
| 填料/增强材料 |
|
| 特性 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | |||
| -- | 1.51 | g/cm³ | ASTM D792 |
| -- | 1.50 | g/cm³ | ISO 1183 |
| 收缩率 | |||
| 流动 : 24小时 | 0.80 到 1.0 | % | ASTM D955 |
| 横向流动 :24小时 | 1.0 到 1.2 | % | ASTM D955 |
| 垂直流动方向 :24小时 | 1.1 | % | ISO 294-4 |
| 流动方向 :24小时 | 0.89 | % | ISO 294-4 |
| 吸水率 (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | |||
| -- 1 | 3450 | MPa | ASTM D638 |
| -- | 3110 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服 | 53.8 | MPa | ASTM D638 |
| 屈服 | 53.0 | MPa | ISO 527-2 |
| 断裂 | 53.8 | MPa | ASTM D638 |
| 断裂 | 53.0 | MPa | ISO 527-2 |
| 伸长率 | |||
| 屈服 | 2.7 | % | ASTM D638 |
| 屈服 | 2.8 | % | ISO 527-2 |
| 断裂 | 2.8 | % | ASTM D638 |
| 断裂 | 2.9 | % | ISO 527-2 |
| 弯曲模量 |