沙特sabic PPS
SABICInnovative Plastics LNP Thermocomp OFM66 PPS
Polyphenylene Sulfide (PPS)
SABIC Innovative Plastics (GE Plastics)
产品说明：
LNP* Thermocomp* OFM66 is a compound based on PolyphenyleneSulfide resin containing Glass Fiber, Mineral. Added features ofthis material include: Low Warpage.
Thisdata was supplied by SABIC-IP for the Americas region.
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.92 g/cc | 0.0694 lb/in³ | ASTM D 792 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 115 MPa | 16700 psi | ASTM D 638 |
| 伸长率 (断裂) | 2.8 % | 2.8 % | ASTM D 638 |
| 弯曲强度 | 172 MPa | 24900 psi | ASTM D 790 |
| 弯曲模量 | 17.94 GPa | 2602 ksi | ASTM D 790 |
| 悬壁梁缺口冲击强度 | 0.370 J/cm @Temperature 23.0 °C | 0.693 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| 悬壁梁无缺口冲击强度 | 1.70 J/cm @Temperature 23.0 °C | 3.18 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 耗散因数 | 0.0020 @Frequency 1.00e+6 Hz | 0.0020 @Frequency 1.00e+6 Hz | ASTM D 150 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(0.46 MPa) | 276 °C @Thickness 3.20 mm | 529 °F @Thickness 0.126 in | unannealed; ASTM D 648 |
| 载荷下热变形温度(1.8 MPa) | 254 °C @Thickness 3.20 mm |
塑胶料 沙特sabic