THERMOPLASTIC POLYESTER ELASTOMER
DuPont Performance Polymers
产品说明:
40 Shore D High Performance Polyester Elastomer withNon-discoloring Stabilizer
物性信息:
基本信息黄卡编号E83247-251124添加剂紫外线稳定剂用途薄膜片材型材形式粒子加工方法薄膜挤出挤出浇铸片材挤出成型热成型型材挤出成型注射成型多点数据CreepModulus vs. Time (ISO 11403-1)Isochronous Stress vs. Strain (ISO11403-1)Isothermal Stress vs. Strain (TPE) (ISO 11403-1)ShearStress vs. Shear Rate (ISO 11403-1)Specific Volume vs Temperature(ISO 11403-2)Viscosity vs. Shear Rate (ISO 11403-2)部件标识代码 (ISO11469)>TPC-ET树脂ID (ISO 1043)TPC-ET物理性能额定值单位制测试方法密度1.11g/cm³ISO1183熔流率(熔体流动速率) (220°C/2.16kg)8.5g/10 minISO 1133溶化体积流率(MVR) (220°C/2.16 kg)9.00cm³/10minISO 1133收缩率
ISO 294-4 垂直流动方向0.80%ISO294-4 流动方向0.80%ISO 294-4吸水率
24 hr0.70%ASTMD570 23°C, 24 hr, 2.00mm0.70%ISO 62 平衡, 23°C, 2.00 mm, 50% RH0.30%ISO62硬度额定值单位制测试方法肖氏硬度
ISO 868 邵氏D37
ISO 868 邵氏 D, 15秒33
ISO 868机械性能额定值单位制测试方法拉伸模量45.0MPaISO 527-2拉伸应力
ISO 527-2 断裂29.0MPaISO527-2 5.0%应变2.40MPaISO 527-2 10% 应变3.20MPaISO527-2 50%应变6.70MPaISO 527-2 **** 应变7.50MPaISO 527-2拉伸应变 (断裂)> 300%ISO 527-2标称拉伸断裂应变800%ISO527-2拉伸蠕变模量
ISO 899-1 1hr28.0MPaISO 899-1 1000 hr21.0MPaISO 899-1弯曲模量45.0MPaISO178抗磨损性180mm³ISO 4649充模分析额定值单位制测试方法Specific Heat Capacity ofMelt2140J/kg/°C
Thermal Conductivity of Melt0.16W/m/K
补充信息额定值单位制测试方法Effective Thermal Diffusivity0.0544cSt
Emission of Organic Compounds10.0µgC/gVDA 277Odor2.5
VDA 270弹性体额定值单位制测试方法撕裂强度
ISO 34-1 横向流量100kN/mISO34-1 流量100kN/mISO 34-1冲击性能额定值单位制测试方法简支梁缺口冲击强度
ISO 179/1eA -40°C无断裂
ISO 179/1eA -30°C无断裂
ISO 179/1eA 23°C无断裂
ISO 179/1eA简支梁无缺口冲击强度
ISO 179/1eU -30°C无断裂
ISO 179/1eU 23°C无断裂
ISO 179/1eU拉伸冲击强度 (23°C)145kJ/m²ISO8256/1热性能额定值单位制测试方法玻璃转化温度 1-55.0°CISO11357-2熔融温度 2193°CISO 11357-3线形热膨胀系数
ISO 11359-2 流动2.3E-4cm/cm/°CISO11359-2 横向2.3E-4cm/cm/°CISO11359-2电气性能额定值单位制测试方法介电强度18kV/mmIEC 60243-1相对电容率
IEC 60250 100Hz4.80
IEC 60250 1MHz4.70
IEC 60250漏电起痕指数600VIEC 60112充模分析额定值单位制测试方法熔体密度1.03g/cm³