ESTANE TPU 2103-70A----Lubrizol Estane®2103-70A产品说明：Formerly Pellethane，Feature: HighMVTR
Available in Americas, Europe, Middle East, Africa, India andAsia
Dataprovided by Lubrizol
Lubrizol acquired the Pellethane product line from Dow in 2009.
TPU 2103-70A物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.06 g/cc | 0.0383 lb/in³ | ASTM D792 |
| 线性成型收缩率,Flow | 0.0040 - 0.0050 cm/cm | 0.0040 - 0.0050 in/in | ASTM D955 |
| 线性成型收缩率，横向 | -0.00300 - 0.0080 cm/cm | -0.00300 - 0.0080 in/in | ASTM D955 |
| 熔体流动速率 | 11 g/10 min@Load 8.70 kg, Temperature 224 °C | 11 g/10 min@Load 19.2 lb, Temperature 435 °F | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 A) | 72 | 72 | ASTM D2240 |
| 极限抗拉强度 | 24.7 MPa | 3580 psi | ASTM D412 |
| 伸长率 (断裂) | 730 % | 730 % | ASTM D412 |
| 50% Modulus | 0.00210 GPa | 0.305 ksi | ASTM D412 |
| 100 模量 | 0.00300 GPa | 0.435 ksi | ASTM D412 |
| 300％模量 | 0.00520 GPa | 0.754 ksi | ASTM D412 |
| 撕裂强度 | 66.5 kN/m | 379 pli | Die C; ASTM D624 |
| 泰伯磨损，毫克/1000次 | 3.0 | 3.0 | H22 Wheel, 1000g; ASTM D1044 |
| 压缩 久变形 | 25 %@Temperature 25.0 °C, Time 79200 sec | 25 %@Temperature 77.0 °F, Time 22.0 hour | ASTM D395, Method B |
| 75 %@Temperature 70.0 °C, Time 79200 sec | 75 %@Temperature 158 °F, Time 22.0 hour | ASTM D395, Method B | |
| Tensile Set | 50 % | 50 % | Elongation set after break; ASTM D412 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 175 µm/m-°C@Temperature 20.0 °C | 97.2 µin/in-°F@Temperature 68.0 °F | ASTM D696 |
| 维卡软化温度 | 75.0 °C | 167 °F | 120°C/hr, 9.8N; ASTM D1525 |
| 玻璃化转变温度，Tg | -69.0 °C | -92.2 °F |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 188 - 204 °C | 370 - 399 °F | Extrusion |
| 193 - 210 °C | 379 - 410 °F | Molding | |
| 模具温度 | 16.0 - 60.0 °C | 60.8 - 140 °F | |
| 干燥温度 | 82.0 - 93.0 °C | 180 - 199 °F | air dew point <-40°C |