Vydyne® R513HPolyamide 66Ascend Performance Materials OperationsLLC13% 玻璃纤维增强材料产品说明：Vydyne R513H is general-purpose, 13%glass-fiber reinforced, heat-stabilized PA66 resin. Available innatural, it is an injection-molding grade resin that is lubricatedfor machine feed, flow, and mold release. Glass-reinforced Vydyneresins provide a higher heat distortion temperature, betterresistance to creep, higher impact, and better dimensionalstability when compared with unreinforced PA66. This product hasgood chemical resistance to a broad range of chemicals, includingmany aliphatic and aromatic hydrocarbons found in most solvents,gasoline, hydraulic fluids, greases and machine oils.
Vydyne R513H has tensile strength and modulus properties just belowaluminum and zinc and can replace these metals in numerousapplications due to an excellent balance of properties. Reductionin production costs, energy consumption and part weight are keyadvantages of Vydyne glass-reinforced PA66 resins over aluminumand/or zinc die-cast parts.
Vydyne R513H is heat-stabilized and formulated to minimize theoxidative and thermal degradation of the PA66 polymer when exposedto elevated temperatures for extended periods of time. Vydyne R513Hprovides improved retention of physical properties under exposureto long-term heat. The continuous operating use temperature is 275°F, with short-term peak temperatures as high as 475° F.
Typical Applications/End Uses:
Vydyne R513H resin has been used for many under-the-hood automotiveapplications, motor housings for power tools and garden appliances.This resin has also been used in miscellaneous brackets, gears andclips, which require high rigidity and strength.物性信息：基本信息
黄卡编号E70062-249082填料/增强材料玻璃纤维增强材料, 13%填料按重量添加剂热稳定剂润滑剂特性刚性，高高强度抗溶剂性良好的流动性耐化学性良好耐汽油性耐油性能耐油脂性能热稳定性润滑脱模性能良好用途齿轮动力/其它工具汽车的发动机罩下的零件外壳机构评级ASTMD 4066 PA0121G15ASTM D 6779PA0121G15UL文件号E70062外观自然色形式粒子加工方法注射成型多点数据Isothermal Stress vs.Strain (ISO 11403-1)物理性能干燥调节后的单位制测试方法密度1.23--g/cm³ISO 1183收缩率
ISO 294-4 垂直流动方向: 23°C, 2.00 mm1.0--%ISO294-4 流动方向 :23°C, 2.00 mm0.50--%ISO 294-4吸水率
ISO 62 23°C, 24hr1.0--%ISO 62 平衡, 23°C, 50% RH2.2--%ISO62机械性能干燥调节后的单位制测试方法拉伸模量 (23°C)62003900MPaISO 527-2拉伸应力 (断裂, 23°C)11575.0MPaISO527-2拉伸应变 (断裂, 23°C)3.013%ISO527-2弯曲模量 (23°C)52003150MPaISO178弯曲应力 (23°C)165106MPaISO178泊松比0.40--
ISO 527-2冲击性能干燥调节后的单位制测试方法简支梁缺口冲击强度
ISO 179 -30°C6.05.3kJ/m²ISO179 23°C6.07.5kJ/m²ISO 179简支梁无缺口冲击强度
ISO 179 -30°C3137kJ/m²ISO179 23°C3842kJ/m²ISO 179悬壁梁缺口冲击强度
ISO 180 -30°C5.05.4kJ/m²ISO180 23°C5.18.5kJ/m²ISO 180热性能干燥调节后的单位制测试方法热变形温度
0.45 MPa,未退火258--°CISO75-2/B 1.8 MPa,未退火240--°CISO 75-2/A熔融温度260--°CISO 11357-3线形热膨胀系数
ISO 11359-2 流动 :23 到 55°C, 2.00 mm3.0E-5--cm/cm/°CISO11359-2 横向 : 23到 55°C, 2.00 mm1.1E-4--cm/cm/°CISO 11359-2RTI Elec
UL 746 0.750mm140--°CUL 746 1.50 mm140--°CUL746 3.00mm140--°CUL 746RTI Imp
UL 746 0.750mm120--°CUL 746 1.50 mm120--°CUL746 3.00mm120--°CUL 746RTI
UL 746 0.750mm125--°CUL 746 1.50 mm140--°CUL746 3.00mm140--°CUL 746电气性能干燥调节后的单位制测试方法体积电阻率 (0.750 mm)1.0E+13--ohms·cmIEC60093介电强度 (1.00 mm)20--kV/mmIEC60243耐电弧性 (3.00 mm)PLC 6--
ASTM D495漏电起痕指数 (3.00 mm)250 到399--VIEC 60112高电弧燃烧指数(HAI)
UL 746 0.750mmPLC 0--
UL 746 1.50mmPLC 0--
UL 746 3.00mmPLC 0--
UL 746高电压电弧起痕速率 (HVTR)PLC 1--
UL 746热丝引燃 (HWI)
UL 746 0.750mmPLC 4--
UL 746 1.50mmPLC 3--
UL 746 3.00mmPLC 4--
UL 746可燃性干燥调节后的单位制测试方法UL 阻燃等级
UL 94 0.750mmHB--
UL 94 1.50mmHB--
UL 94 3.00mmHB--
UL 94灼热丝易燃指数
IEC 60695-2-12 0.750 mm675--°CIEC60695-2-12 1.50mm675--°CIEC60695-2-12 3.00mm675--°CIEC 60695-2-12热灯丝点火温度
IEC 60695-2-13 0.750 mm700--°CIEC60695-2-13 1.50mm700--°CIEC60695-2-13 3.00mm700--°CIEC 60695-2-13极限氧指数25--%ISO 4589-2注射干燥单位制
干燥温度80.0°C
干燥时间4.0hr
建议的*大回制料比例25%
料筒后部温度280 到 310°C
料筒中部温度280 到 310°C
料筒前部温度280 到 310°C
射嘴温度280 到 310°C
加工（熔体）温度285 到 305°C
模具温度65.0 到 95.0°C
VYDYNE® R530H 尼龙66。VYDYNE® R530H 尼龙66 用途： 汽车部件特性备注：抗冻； 抗溶剂性；良好的流动性； 耐化学性良好； 耐疲劳性能； 耐汽油性； 耐水解性； 热稳定性； 润滑重要参数： 密度:1.37 g/cm3吸水率:0.9 % 成型收缩率:0.4 % 弯曲强度:270 MPa 弯曲模量:9100 MPa 维卡软化点:252 ℃热变形温度:245℃Vydyne®R530H尼龙树脂是通用的聚酰胺，热稳定，抗水解，30％的玻璃纤维增强树脂。它是专门设计来**化物理性质的保留时在高温下暴露于防冻液的解决方案。本产品还润滑，以提高机床的进给和流量。也可用：泛达530HNAT，泛达530H NT，泛达530H黑色，泛达530H BK02，泛达530H BK0201，泛达530HBK0202和泛达530HBK08。当与未增强尼龙6,6相比玻璃增强Vydyne®树脂提供较高的热变形温度，抗蠕变和更好的尺寸稳定性。这些产品具有到范围广泛的化学品，包括汽油，液压流体和大部分溶剂具有良好的耐化学性。Vydyne®R530H是热稳定的，当暴露于高温中的服务，以尽量减少聚合物的氧化降解。此产品提供了下暴露于长期热物理性能改进的保持。另外，Vydyne®R530H具有优良的针织线的强度和耐疲劳性，这是防冻溶液循环试验是必不可少的。Vydyne®R530H应用：已用于几个下引擎罩汽车应用。水解等性能使其成为一个很好的候选人，散热器端部容器和加热器的核心应用代理及经销工程塑料和通用塑料。在供应PA66美国首诺 R533H 度 耐水解，食品级供应PA66 美国首诺 R543H HB耐热性供应PA66 美国首诺 21SPC 通用级V-2供应PA66 美国首诺 M344 BK 阻燃性 韧性供应PA66 美国首诺 50BWFS 通用级