Hostaform® C 9021 GV1/30
Acetal (POM) Copolymer
Celanese Corporation
26% 玻璃纤维增强材料
产品说明：
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 02-003, GF26
POM copolymer
Injection molding type, reinforced with ca 26 % glass fibers;high
resistance to thermal and oxidative degradation; reducedthermal
expansion and shrinkage.
UL-registration for all colours and a thickness more than 1.57 mmas
UL 94 HB, temperature index UL 746 B electrical 105°C,mechanical
95°C (tensile impact) and 100°C (tensile).
Burning rate ISO 3795 and FMVSS 302 < 100 mm/min and athickness
more than 1 mm thickness.
Ranges of applications: For molded parts with very highstrength
and rigidity as well as higher hardness.
FMVSS = Federal Motor Vehicle Safety Standard (USA)
UL = Underwriters Laboratories (USA)
物性信息：
| 基本信息 |
|
|---|
| 黄卡编号 | |
| 填料/增强材料 | |
| 特性 | |
| RoHS 合规性 | |
| 加工方法 | |
| 多点数据 | Isothermal Stress vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1)
|
| 树脂ID (ISO 1043) | |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 密度 | 1.60 | g/cm³ | ISO 1183 |
| 溶化体积流率（MVR） (190°C/2.16 kg) | 4.00 | cm³/10min | ISO 1133 |
| 吸水率 (饱和, 23°C) | 0.90 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 拉伸模量 | 9200 | MPa | ISO 527-2/1A/1 |
| 拉伸应力 (断裂) | 135 | MPa | ISO 527-2/1A/5 |
| 拉伸应变 (断裂) | 2.5 | % | ISO 527-2/1A/5 |
| 拉伸蠕变模量 |
|
| ISO 899-1 |
| 1 hr | 7700 | MPa | ISO 899-1 |
| 1000 hr | 5400 | MPa | ISO 899-1 |
| 弯曲模量 (23°C) | 7800 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 简支梁缺口冲击强度 |
|
| ISO 179/1eA |
| -30°C | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 8.0 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 |
|
| ISO 179/1eU |
| -30°C | 35 | kJ/m² | ISO 179/1eU |
| 23°C | 30 | kJ/m² | ISO 179/1eU |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 热变形温度 |
|
|
|
| 1.8 MPa, 未退火 | 160 | °C | ISO 75-2/A |
| 8.0 MPa, 未退火 | 125 | °C | ISO 75-2/C |
| 熔融温度 1 | 166 | °C | ISO 11357-3 |
| 线形热膨胀系数 |
|
| ISO 11359-2 |
| 流动 | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| 横向 | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 表面电阻率 | 1.0E+14 | ohms | IEC 60093 |
| 体积电阻率 | 1.0E+14 | ohms·cm | IEC 60093 |
| 介电强度 | 40 | kV/mm | IEC 60243-1 |
| 相对电容率 |
|
| IEC 60250 |
| 100 Hz | 4.30 |
| IEC 60250 |
| 1 MHz | 4.30 |
| IEC 60250 |
| 耗散因数 |
|
| IEC 60250 |
| 100 Hz | 3.0E-3 |
| IEC 60250 |
| 1 MHz | 6.0E-3 |
| IEC 60250 |
| 漏电起痕指数 | 600 | V | IEC 60112 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|
| UL 阻燃等级 |
|
| UL 94 |
| 1.57 mm | HB |
| UL 94 |
| 3.18 mm | HB |
| UL 94 |
| 充模分析 | 额定值 | 单位制 | 测试方法 |
|---|
| Density of Melt | 1.350 | g/cm³ | 内部方法 |
| Ejection Temperature | 164 | °C | 内部方法 |
| Specific Heat Capacity of Melt | 1810 | J/kg/°C | 内部方法 |
| Thermal Conductivity of Melt | 0.22 | W/m/K | 内部方法 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
|---|
| Effective Thermal Diffusivity | 0.0651 | cSt | 内部方法 |
| 注射 | 额定值 | 单位制 |
|
|---|
| 干燥温度 | 100 到 120 | °C |
|
| 干燥时间 | 3.0 到 4.0 | hr |
|
| 建议的*大水分含量 | 0.15 | % |
|
| 料斗温度 | 20.0 到 30.0 | °C |
|
| 料筒后部温度 | 170 到 180 | °C |
|
| 料筒中部温度 | 180 到 190 | °C |
|
| 料筒前部温度 | 190 到 200 | °C |
|
| 射嘴温度 | 190 到 210 | °C |
|
| 加工（熔体）温度 | 190 到 210 | °C |
|
| 模具温度 | 80.0 到 120 | °C |
|
| 注塑压力 | 60.0 到 120 | MPa |
|
| 注射速度 | 慢 |
|
|
| 保压 | 60.0 到 120 | MPa |
|
| 背压 | 0.00 到 2.00 | MPa |
|
| 注射说明 |
|---|
| Manifold Temperature: 190 to 210°CZone 4 Temperature: 190to 210°CFeed Temperature: 60 to 80°C |
耐候型POM?产品性能及应用?
POM是线性聚合物，高度结晶，分子主链为C一0键，对波长在280～400?nm范围内的紫外光敏感。紫外线的短波长、高频率使其具有很高的能量，当照射到POM分子链上时，容易将高分子链切断，使生产中已封端的POM出现不稳定自由基，从而引发降解反应。紫外光照射是POM老化的主要因素，改善POM的耐紫外光老化性能是改善POM稳定性和耐候性的关键所在。目前提高POM耐紫外光性能的方法主要是添加光稳定剂，包括光屏蔽剂、紫外线吸收剂、猝灭剂和受阻胺类光稳定剂等?。各POM生产商(除国内云天化、蓝星及LG外)都针对户外使用的POM开发了光稳定POM产品......我司还供应以下产品:
供应 德国赫斯特 POM C9021GV1/30
供应 德国赫斯特 POM MT8R02
供应 德国赫斯特 POM C9021GV3/10 33
供应 德国泰科纳 POM C13031
供应 德国泰科纳 POM C2521
供应 德国泰科纳 POM C27021
供应 德国泰科纳 POM C9021
供应 德国泰科纳 POM C9021GV1/20
供应 德国泰科纳 POM S 27072 WS 10/1570
本公司郑重承诺：所售产品原厂原包
供应/ 美国杜邦 POM /520MP NC010 (20% Teflon® PTFE)101.50元/千克