Bayblend PC/ABS FR 2000---产品说明：Easy-flowing FR grade. Flameretardant grade with antimony, chlorine and bromine free, flameretardant package, optimized processability.
Applications: Housings for office e,electrical engineering, computer sectors.
Information provided by Bayer.
PC/ABS FR 2000物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.18 g/cc | 0.0426 lb/in³ | |
| 吸水率 | 0.70 % | 0.70 % | Saturation in water |
| 平衡吸湿 | 0.20 % | 0.20 % | E at 50% RH |
| 饱和吸水率 | 0.70 % | 0.70 % | |
| 线性成型收缩率 | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| 熔体流动速率 | 30 g/10 min @Load 5.00 kg, Temperature 240 °C | 30 g/10 min @Load 11.0 lb, Temperature 464 °F | |
| Spiral Flow | 76.0 cm @Thickness 2.50 mm | 29.9 in @Thickness 0.0984 in | at 254°C melt temp. |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 极限抗拉强度 | 45.0 MPa | 6530 psi | ASTM D638 |
| 抗张强度(屈服) | 60.0 MPa | 8700 psi | |
| 伸长率 (断裂) | 70 % | 70 % | ASTM D638 |
| 屈服伸长率 | 4.0 % | 4.0 % | |
| 拉伸模量 | 2.70 GPa | 392 ksi | |
| 弯曲强度 | 95.0 MPa | 13800 psi | at 5% strain; ASTM D790 |
| 弯曲模量 | 2.70 GPa | 392 ksi | ASTM D790 |
| 悬壁梁缺口冲击强度 | 4.30 J/cm @Thickness 3.20 mm | 8.06 ft-lb/in @Thickness 0.126 in | ASTM D256 |
| 冲击试验 | 49.0 J @Thickness 3.20 mm | 36.1 ft-lb @Thickness 0.126 in | Instrumented Total Impact; 3.2 mm thick, 12.5 mm dart, 75 mm clamp,6.7 m/s; ASTM D3763 |