HANWHACHNA-8380
High Density (HMW) Polyethylene
Hanwha Chemical
产品说明：
Hanwha CHNA-8380 is a high molecular weight, high densitypolyethylene(HDPE) insulation compound especially designed forhigh-speed wire insulating extrusion process. It provides excellentprocessability, environmental and thermal stress crackingresistance. It meets major international aging test specificationfor both solid and foam/skin insulation. It can be used for thefull range of telephone cable insulation including air-core,jelly-filled and LAN cable (Cat. 5/5e).
物性信息：
| 基本信息 |
|
|---|
| 特性 | 高 ESCR（抗应力开裂） 高分子量 高密度 可加工性，良好
|
| 用途 | |
| 机构评级 | ASTM D 1248, III, Class A, Cat. 4, Grade E8 ASTM D 1248, III, Class A, Cat. 4, Grade E9 BS 6234 Type H03 ICEA S-84-608 IEC 60708 NF C 32-060
|
| 形式 | |
| 加工方法 | |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 密度 | 0.945 | g/cm³ | ASTM D1505 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| 抗环境应力开裂 (50°C, 10% Igepal,F0) | > 1000 | hr | ASTM D1693 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|
| 肖氏硬度 (邵氏 D, 1 秒) | 53 |
| ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 抗张强度 | 23.5 | MPa | ASTM D638 |
| 伸长率 (断裂) | 550 | % | ASTM D638 |
| 老化 | 额定值 | 单位制 | 测试方法 |
|---|
| Oven Aging (100°C) | 2.0 | day |
|
| 拉伸强度保持率 - 2 days (100°C) | > 90 | % | ASTM D638 |
| 伸长保持率 - 2 days (100°C) | > 90 | % | ASTM D638 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 耐热应力裂纹 | > 96 | hr | ASTM D2951 |
| 氧感应时间 - AI (200°C) | > 100 | min | ASTM D3895 |
| 脆化温度 | < -76.0 | °C | ASTM D746 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 体积电阻率 | > 1.0E+16 | ohms·cm | ASTM D257 |
| 介电常数 (1 MHz) | < 2.30 |
| ASTM D150 |
| 耗散因数 (1 MHz) | < 1.0E-4 |
| ASTM D150 |