食品接触级LDPE LD 100AC埃克森美孚---Product Description: LD 100 series areLDPE grades, offering a good balance of optical and mechanicalproperties. Several additive packages are available according tothe required surface properties.
Availability: Africa & Middle East, Asia Pacific and Europe
Additive:
Antiblock: 450 ppm
Slip: 500 ppm
Thermal Stabilizer: Yes
Applications:
Blend Partner
Cast Film
Compounding
Foams
Food packaging
Form Fill and Seal Packaging
Freezer Film
Lamination Film
Light Duty Shrink Film
Liners
Mail Bag
Produce Bags
Shoppers
Textile Packaging
Tough Medium Sized Molding
Information provided by ExxonMobil
LDPE LD 100AC物性信息:
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
密度 | 0.923 g/cc | 0.0333 lb/in³ | ExxonMobil method |
熔体流动速率 | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
Antiblock Level | 450 ppm | 450 ppm | |
Slip Level | 500 ppm | 500 ppm |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
抗张强度(MD : 屈服) | 11.0 MPa | 1600 psi | ASTM D882 |
抗张强度(TD : 屈服) | 11.0 MPa | 1600 psi | ASTM D882 |
断裂伸长率,MD | 330 % | 330 % | ASTM D882 |
断裂伸长率,TD | 550 % | 550 % | ASTM D882 |
埃尔曼多夫抗撕强度(MD) | 150 g | 150 g | ASTM D1922 |
埃尔曼多夫抗撕强度(TD) | 120 g | 120 g | ASTM D1922 |
落锤试验 | 80.0 g | 0.176 lb | ASTM D1709A |
抗张强度(MD : 断裂) | 24.8 MPa | 3600 psi | ASTM D882 |
抗张强度(TD : 断裂) | 22.1 MPa | 3200 psi | ASTM D882 |
割线模量(1% 正割 MD) | 207 MPa | 30000 psi | ASTM D882 |
割线模量(1% 正割 TD) | 228 MPa | 33000 psi | ASTM D882 |