PA66美国杜邦,72G13HS1L高强度耐高温
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
基本性能 | 吸水率 | 饱和(23℃) | ASTM D-570 | 4.6 | % |
吸水率 | 24小时浸渍(23℃) | ASTM D-570 | 0.5 | % | |
物理性能 | 比重 | ASTM D-792 | 1.35 | ||
机械性能 | 洛氏硬度R | DAM | ASTM D-785 | R122 | |
挠曲模量 | 23℃,50%RH | ASTM D-790 | 5516 | MPa | |
挠曲模量 | 23℃,DAM | ASTM D-790 | 6895 | MPa | |
埃佐冲击强度 | 23℃,50%RH | ASTM D-256 | 128 | j/m | |
断裂伸长率 | 23℃,50%RH | ASTM D-638 | 4 | % | |
挤剪强度 | 23℃,DAM | ASTM D-732 | 72 | MPa | |
洛氏硬度M | 50%RH | ASTM D-785 | M90 | ||
洛氏硬度M | DAM | ASTM D-785 | M96 | ||
断裂伸长率 | 23℃,DAM | ASTM D-638 | 3 | % | |
洛氏硬度R | 50%RH | ASTM D-785 | R118 | ||
泰伯磨耗量 | 50%RH | 36 | cycles | ||
挠曲强度 | 23℃,DAM | ASTM D-790 | 228 | MPa | |
埃佐冲击强度 | 23℃,DAM | ASTM D-256 | 128 | j/m | |
拉伸强度 | 23℃,DAM | ASTM D-638 | 151.6 | MPa | |
拉伸强度 | 23℃,50%RH | ASTM D-638 | 110.3 | MPa |