| 日本东丽 PBT 1184G-30技术参数 |
| 性能项目 | 试验条件 | 测试 | 测试数据 | |
| 比重 | ASTM D792 | 1.65 | ||
| 吸水率 | 23℃,65%RH 24H | ASTM D570 | 0.07 | % |
| 拉伸强度 | 23℃ | ASTM D638 | 145 | MPa |
| 伸长率 | ASTM D638 | 4 | % | |
| 弯曲强度 | ASTM D790 | 215 | MPa | |
| 弯曲模量 | ASTM D790 | 9.4 | Gpa | |
| Izod缺口冲击强度 | 23℃ | ASTM D256 | 62 | J/m |
| 洛氏硬度 | ASTM D785 | 87 | M | |
| 摩擦系数 | -，对金属 | ASTM D1894 | 0.15 | |
| 摩擦系数 | -，对本身 | ASTM D1894 | 0.20 | |
| 体积电阻率 | ASTM D257 | 2.5 | ||
| 耐电压 | ASTM D149 | 27 | MV/m | |
| 介电常数 | -，50Hz | ASTM D150 | 4.0 | |
| 介电常数 | -，10 | ASTM D150 | 3.8 | |
| 介质损耗角正切 | -，50Hz | ASTM D150 | 0.001 | |
| 介质损耗角正切 | -，10 | ASTM D150 | 0.01 | |
| 电弧电阻系数 | ASTM D495 | 123 | Sec | |
| 热变形温度 | -，0.45Mpa | ASTM D648 | 223 | ℃ |
| 热变形温度 | -，1.82Mpa | ASTM D648 | 210 | ℃ |
| 线膨胀系数 | ASTM D696 | 4.1 | ×10 | |
| 阻燃性 | UL94 | V-0 | ||