原装出售 UBE UBESTA® 3020IX1 Rigid Automotive Grade Nylon 12物性表
UBE UBESTA®3020IX1 Rigid Automotive Grade Nylon 12
Polymer,Thermoplastic,Nylon,Nylon 12
UBE
产品说明:
Description: UBEUBESTA® Automotive grade Nylon 12
Comments: conductive,impact modified
Information provided by UBE.
UBE UBESTA® 3020IX1 Rigid Automotive Grade Nylon 12 物性表
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
密度 | 1.01 g/cc | 0.0365 lb/in³ | ASTM D792 |
熔体流动速率 | 12 g/10 min @Load 2.16 kg, Temperature 235 °C | 12 g/10 min @Load 4.76 lb, Temperature 455 °F | ASTM D1238R |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
肖氏硬度 (邵氏 D) | 71 | 71 | ASTM D2240 |
抗张强度(断裂) | >= 40.0 MPa | >= 5800 psi | ASTM D638 |
抗张强度(屈服) | 29.0 MPa | 4210 psi | ASTM D638 |
伸长率 (断裂) | 140 % | 140 % | ASTM D638 |
弯曲强度 | 31.0 MPa | 4500 psi | ASTM D790 |
弯曲模量 | 0.870 GPa | 126 ksi | ASTM D790 |
悬壁梁缺口冲击强度 | 4.50 J/cm | 8.43 ft-lb/in | ASTM D256 |
电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
体积电阻率 | 1.00e+6 - 1.00e+7 ohm-cm | 1.00e+6 - 1.00e+7 ohm-cm |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
熔融温度 | 178 °C | 352 °F | ASTM D3418 |
加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
加工温度 | 230 °C | 446 °F | Flange Temperature for T-Die Cast Film Extrusion |
进料温度 | 40.0 °C | 104 °F | Injection Molding |
1区 | 190 °C | 374 °F | For T-Die Cast Film Extrusion |
230 °C | 446 °F | For 8x1 mm Tube Extrusion | |
2区 | 210 °C | 410 °F | For T-Die Cast Film Extrusion |
225 °C | 437 °F | For 8x1 mm Tube Extrusion | |
3区 | 220 °C | 428 °F | For 8x1 mm Tube Extrusion |
230 °C | 446 °F | For T-Die Cast Film Extrusion | |
4区 | 215 °C | 419 °F | For 8x1 mm Tube Extrusion |
模具温度 | 230 °C | 446 °F | For T-Die Cast Film Extrusion |
40.0 - 60.0 °C | 104 - 140 °F | Injection Molding | |
射速 | 100 mm/sec | 3.94 in/sec | Injection Molding |
Die Opening | 0.0400 cm | 0.0157 in | For T-Die Cast Film Extrusion |
Roll Temperature | 50.0 °C | 122 °F | Chill Roll Temperature for T-Die Cast Film Extrusion |
干燥温度 | 80.0 °C | 176 °F | Option 1 |
100 °C | 212 °F | Option 2 | |
110 °C | 230 °F | Option 3 | |
干燥时间 | 2 - 4 hour | 2 - 4 hour | Option 3 |
4 - 6 hour | 4 - 6 hour | Option 2 | |
6 - 8 hour | 6 - 8 hour | Option 1 | |
注射压力 | 40.0 - 50.0 MPa | 5800 - 7250 psi | Injection Molding (Injection pressure should be increased whenmolding thin wall parts. Pressure up to 75 bar can be usedhere.) |
保压 | 25.0 - 50.0 MPa | 3630 - 7250 psi | Injection Molding |
背压 | 5.00 MPa | 725 psi | Injection Molding |
螺杆转速 | 15 - 76 rpm | 15 - 76 rpm | For 8x1 mm Tube Extrusion |
材料描述 | 测试方法 | |
---|---|---|
C/R | 3-3.5:1 | For 8x1 mm Tube Extrusion |
Calibrating Vacuum | 100 mbar | For 8x1 mm Tube Extrusion |
Calibration | 9.95 mm | For 8x1 mm Tube Extrusion |
Compression Ratio | 2.5-3.5:1 | Injection Molding |
min 3:1 | For 8x1 mm Tube Extrusion | |
Die Diameter | 16 mm | For 8x1 mm Tube Extrusion |
Die Width | 300 mm | For T-Die Cast Film Extrusion |
Extruder | Barmag, Screw Diameter = 30 mm | For T-Die Cast Film Extrusion |
Extruder Characteristics | 65 mm screw diameter | For 8x1 mm Tube Extrusion |
Film Thickness | 60 microns | For T-Die Cast Film Extrusion |
Flight Depth in the Feeding Zone | 10-15% of Screw Diameter | Injection Molding |
Flight Depth in the Metering Zone | 5-7% of Screw Diameter | Injection Molding |
Haul Off Speed | 5 m/min | For T-Die Cast Film Extrusion |
Haul Speed | 10-55 m/min | For 8x1 mm Tube Extrusion |
L/D Ratio | 25:1 | For 8x1 mm Tube Extrusion |
min 20:1 | Injection Molding | |
Length of Compression Zone | 25-45% of total screw length | Injection Molding |
30% of screw length | For 8x1 mm Tube Extrusion | |
Length of Feeding Zone | 20-40% of total screw length | Injection Molding |
30-40% of screw length | For 8x1 mm Tube Extrusion | |
Length of Metering Zone | 30-45% of screw length | For 8x1 mm Tube Extrusion |
35-45% of total screw length | Injection Molding | |
Mandrel Diameter | 12 mm | For 8x1 mm Tube Extrusion |
Peripheral screw speed | 10 m/min | Injection Molding |
Water Temperature | 10-18°C |
UBE UBESTA® 3020IX1Rigid Automotive Grade Nylon 12物性表