现货 德国科思创 PC Apec 1697 良好的流动性聚碳酸酯塑料

PhysicalProperties物理性能

Metric公制数据

English英制数据

Comments测试方法

Density密度 

1.18 g/cc

0.0426 lb/in³

ISO 1183-1

Moisture Absorption at Equilibrium吸湿平衡 

0.120 %

ISO 62, 50% RH

Water Absorption at Saturation饱和水吸收率 

0.300 %

ISO 62

Melt Flow熔融指数 

46.g/10min
@Load 2.16 kg,
Temperature 330 °C0 

46.0 g/10 min
@Load 4.76 lb,
Temperature 626 °F

ISO 1133

MechanicalProperties力学性能

Tensile Strength, Yield屈服拉伸强度 

68.0 MPa

9860 psi

50 mm/min; ISO 527-1,-2

Elongation at Break断裂伸长率

>= 50.0 %

Nominal, 50 mm/min; ISO 527-1,-2

Elongation at Yield屈服伸长率 

6.20 %

Tensile Modulus拉伸模量 

2.40 GPa

348 ksi

1 mm/min; ISO 527-1,-2

Charpy Impact Unnotched夏比缺口试样冲击 

NB
@Temperature 23.0 °C

NB
@Temperature 73.4 °F

ISO 179-1eU

NB
@Temperature -30.0 °C

NB
@Temperature -22.0 °F

ElectricalProperties电性能

Volume Resistivity体积电阻率 

1.00e+17 ohm-cm

IEC 60093

Surface Resistance表面电阻 

1.00e+16 ohm

Dielectric Constant介电常数

2.90
@Frequency 1.00e+6 Hz

IEC 60250

3.00
@Frequency 100 Hz

3.00
@Frequency 100 Hz

Dielectric Strength介电强度 

35.0 kV/mm
@Thickness 1.00 mm

889 kV/in
@Thickness 0.0394 in

IEC 60243-1

Dissipation Factor耗散因数 

0.00100
@Frequency 100 Hz

0.00900
@Frequency 1.00e+6 Hz

0.00900
@Frequency 1.00e+6 Hz

Comparative Tracking Index跟踪指数 

125 V

CTI M; Solution B; IEC 60112

250 V

250 V

Solution A; IEC 60112

ThermalProperties热性能

CTE, linear, Parallel to Flow线性热膨胀系数 

65.0 µm/m-°C
@Temperature 23.0 - 55.0 °C

36.1 µin/in-°F
@Temperature 73.4 - 131 °F

ISO 11359-1,-2

CTE, linear, Transverse to Flow 线性热膨胀系数 

Maximum Service Temperature, Air高使用温度 

200 °C

392 °F

Deflection Temperature at热变形温度 0.46 MPa (66 psi) 

149 °C

300 °F

ISO 75-1,-2

Deflection Temperature at热变形温度 1.8 MPa (264 psi) 

137 °C

279 °F

Vicat Softening Point维卡软化点 

157 °C
@Load 5.10 kg

315 °F
@Load 11.2 lb

120°C/h; ISO 306

Minimum Service Temperature, Air低使用温度

-30.0 °C

-22.0 °F

UL RTI, Electrical相对温度指数 

140 °C

284 °F

UL 746B

UL RTI, Mechanical with Impact机械冲击热指数 

130 °C

266 °F

UL RTI, Mechanical without Impact无机械冲击热指数 

Flammability, UL94 阻燃等级 

HB
@Thickness 1.50 mm

HB
@Thickness 0.0591 in

HB
@Thickness 3.00 mm

HB
@Thickness 0.118 in

OpticalProperties光学性能

ReFRactive Index折射率 

1.578

Procedure A; ISO 489

TRansmission, Visible透光率 

89.0 %
@Thickness 1.00 mm

89.0 %
@Thickness 0.0394 in

ISO 13468-2

ProcessingProperties加工性能

Melt Temperature熔体温度 

330 °C

626 °F

Injection molding; ISO 294

Mold Temperature模温 

100 °C

212 °F

Injection Velocity注射速度 

200 mm/sec

7.87 in/sec

ISO 294