普立万PP 301 Black 1284-11 S--FR flame-retardant polyolefincompounds and masterbatches meet stringent flammability performancerequirements defined by industry agencies, including UnderwritersLaboratories UL 94 V-2, V-0, and 5VA performance ratings. Inaddition, many compounds in the Maxxam FR portfolio offer elevatedRelative Thermal Index (RTI) ratings.
Information provided by PolyOne
PolyOne Maxxam™ FR PP 301 Black 1284-11 S Polypropylene,Unspecified (PP, Unspecified) 物性表
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
比重 | 0.978 g/cc | 0.978 g/cc | ASTM D792 |
熔体流动速率 | 4.0 - 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 4.0 - 12 g/10 min @Load 4.76 lb, Temperature 446 °F | Procedure A; ASTM D1238 |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
抗张强度(屈服) | 31.0 MPa | 4500 psi | Type I, 51 mm/min; ASTM D638 |
伸长率 (断裂) | 230 % | 230 % | Type I, 51 mm/min; ASTM D638 |
弯曲模量 | 1.03 GPa | 149 ksi | ASTM D790 |
悬壁梁缺口冲击强度 | 0.270 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 0.506 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
载荷下热变形温度(0.46 MPa) | 90.0 °C @Thickness 3.18 mm | 194 °F @Thickness 0.125 in | Unannealed; ASTM D648 |
可燃性(UL94) | V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | NC and Black; UL 94 |
V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | NC and Black; UL 94 | |
V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | NC and Black; UL 94 |