PA6 德国巴斯夫 8202C 特性低粘度结晶均聚物可加工性
吸水率
24hr1.6--%ASTM D570 23°C, 24 hr1.6--%ISO62 饱和9.3--%ASTMD570 饱和,23°C9.3--%ISO 62 平衡, 50% RH2.6--%ASTMD570 平衡, 23°C,50% RH2.6--%ISO 62硬度干燥调节后的单位制测试方法洛氏硬度 (R 级)120--
ASTM D785机械性能干燥调节后的单位制测试方法拉伸模量
ISO 527-2 -40°C4090--MPaISO527-2 23°C37001360MPaISO527-2 80°C750--MPaISO527-2 120°C550--MPaISO527-2 150°C445--MPaISO 527-2抗张强度
屈服,-40°C137142MPaASTM D638, ISO527-2 屈服,23°C90.048.0MPaASTMD638 屈服,80°C40.030.0MPaASTM D638, ISO527-2 屈服,121°C30.025.0MPaASTMD638 屈服,23°C88.043.0MPaISO527-2 屈服,120°C30.025.0MPaISO527-2 屈服,150°C25.0--MPaISO527-2 断裂,-40°C13080.0MPaASTMD638 断裂,23°C90.070.0MPaASTMD638 断裂,80°C35.030.0MPaASTMD638 断裂,121°C25.020.0MPaASTM D638伸长率
屈服,-40°C3.03.0%ASTMD638 屈服,23°C4.022%ASTM D638, ISO527-2 屈服,80°C2525%ASTM D638 屈服, 121°C2730%ASTMD638 断裂,-40°C5.03.0%ASTM D638标称拉伸断裂应变
ISO 527-2 -40°C5.03.0%ISO527-2 23°C7.0> 50%ISO 527-2弯曲模量
-40°C33704200MPaASTMD790 23°C3170970MPaASTMD790 65°C600--MPaASTMD790 90°C440--MPaASTMD790 121°C385--MPaASTMD790 23°C2800--MPaISO 178弯曲强度
-40°C183168MPaASTMD790 23°C11042.0MPaASTMD790 65°C30.0--MPaASTMD790 121°C21.0--MPaASTMD790 23°C95.0--MPaISO178冲击性能干燥调节后的单位制测试方法简支梁缺口冲击强度 (23°C)3.5--kJ/m²ISO179简支梁无缺口冲击强度 (23°C)无断裂--
ISO 179悬壁梁缺口冲击强度
ASTM D256 -40°C3221J/mASTMD256 23°C48170J/mASTM D256热性能干燥调节后的单位制测试方法载荷下热变形温度
0.45 MPa,未退火190--°CASTMD648 0.45 MPa,未退火165--°CISO75-2/B 1.8 MPa,未退火75.0--°CASTMD648 1.8 MPa,未退火65.0--°CISO 75-2/A熔融峰值温度220--°CASTM D3418, ISO3146线形热膨胀系数 - 流动8.1E-5--cm/cm/°CASTM E831RTI Elec
UL 746 0.71mm125--°CUL 746 1.5 mm125--°CUL746 3.0mm125--°CUL 746 6.0 mm125--°CUL 746RTI Imp
UL 746 0.71mm65.0--°CUL 746 1.5 mm75.0--°CUL746 3.0mm75.0--°CUL 746 6.0 mm75.0--°CUL 746RTI
UL 746 0.71mm65.0--°CUL 746 1.5 mm85.0--°CUL746 3.0mm85.0--°CUL 746 6.0 mm85.0--°CUL 746电气性能干燥调节后的单位制测试方法体积电阻率
1.50mm> 1.0E+13--ohms·cmASTMD257 --> 1.0E+13--ohms·cmIEC60093介电强度 1(1.50mm)30--kV/mmASTM D149漏电起痕指数600--VIEC 60112可燃性干燥调节后的单位制测试方法UL阻燃等级
UL 94 0.71mmV-2--
UL 94 1.5mmV-2--
UL 94 3.0mmV-2--
UL 94 6.0mmV-2--
UL 94