6330 物性表
| 物理性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 比重 | 1.64 | ASTM D-792 | |
| 模具收缩率 (3.2mm(0.126in)) | 0.5 | % | ASTM D-955 |
| 机械性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 弯曲强度 (3.2mm(0.125in),23℃(73℉)) | 125 | MPa | ASTM D-790 |
| 断裂伸长率 (3.2mm(0.125in),23℃(73℉)) | 4 | % | ASTM D-638 |
| 弯曲模量 | ASTM D-790 | ||
| (3.2mm(0.125in),23℃(73℉)) | 9600 | MPa | |
| (3.2mm(0.125in),23℃(73℉)) | 9600 | MPa | |
| (0.8mm(0.032in),23℃(73℉)) | 13900 | MPa | |
| 拉伸模量 (1.6mm(0.063in),23℃(73℉)) | 11569 | MPa | ASTM D-638 |
| 拉伸强度 (1.6mm(0.063in),23℃(73℉)) | 141 | MPa | ASTM D-638 |
| 断裂伸长率 (1.6mm(0.063in),23℃(73℉)) | 3.3 | % | ASTM D-638 |
| 压缩模量 | 4100 | MPa | ASTM D-695 |
| 弯曲强度 (3.2mm(0.125in),23℃(73℉)) | 125 | MPa | ASTM D-790 |
| IZOD冲击强度 (3.2mm(0.126in)) | 160 | J/m | ASTM D-256 |
| 断裂伸长率 (3.2mm(0.125in),23℃(73℉)) | 4 | % | ASTM D-638 |
| 拉伸模量 | ASTM D-638 | ||
| (3.2mm) | 10500 | MPa | |
| (1.6mm(0.063in),23℃(73℉)) | 11569 | MPa | |
| 压缩模量 | 4100 | MPa | ASTM D-695 |
| 弯曲强度 (0.8mm(0.032in),23℃(73℉)) | 158 | MPa | ASTM D-790 |
| 弯曲模量 (0.8mm(0.032in),23℃(73℉)) | 13900 | MPa | ASTM D-790 |
| 拉伸模量 (3.2mm(0.125in),23℃(73℉)) | 10500 | MPa | ASTM D-638 |
| IZOD冲击强度 (3.2mm(0.126in)) | 160 | J/m | ASTM D-256 |
| 弯曲强度 (0.8mm(0.032in),23℃(73℉)) | 158 | MPa | ASTM D-790 |
| 拉伸强度 (3.2mm(0.125in),23℃(73℉)) | 125 | MPa | ASTM D-638 |