机械性能 | 拉伸强度 | 23℃ | ASTM D638 | 120 | MPa | |
伸长率 | 23℃ | ASTM D638 | 4 | % | ||
弯曲强度 | 23℃ | ASTM D790 | 140 | MPa | ||
弯曲模量 | 23℃ | ASTM D790 | 6.3 | Gpa | ||
Izod缺口冲击强度 | 缺口 | 23℃ | ASTM D256 | 60 | J/M | |
无缺口 | 23℃ | ASTM D256 | 20 | KJ/m2 | ||
洛氏硬度 | ASTM D785 | 88 | M | |||
摩擦系数 | - | 对金属 | ASTM D1894 | 0.15 | ||
- | 对本身 | ASTM D1894 | 0.20 | |||
电气性能 | 体积电阻率 | ASTM D257 | 1.4 | |||
耐电压 | ASTM D149 | 25 | MV/m | |||
介电常数 | - | 50Hz | ASTM D150 | 3.6 | ||
- | 106Hz | ASTM D150 | 3.8 | |||
介电损耗正切值 | - | 50Hz | ASTM D150 | 0.002 | ||
- | 106Hz | ASTM D150 | 0.02 | |||
PBT日本宝理2002K - 润滑级,添加PTFE润滑
PBT日本宝理2002U 耐候性好
PBT日本宝理2016 阻燃等级V-0
PBT日本宝理201AC 阻燃HB
PBT日本宝理201NF 无卤阻燃V-0
PBT日本宝理209AW 阻燃等级V-0,级
PBT日本宝理300FP 高流动,挤出成型
PBT日本宝理303RA 30%玻纤增强,附着力强
PBT日本宝理304SA 15%玻纤增强,抗翘曲,
PBT日本宝理3100H 7.5%玻纤增强,良好的韧性
PBT日本宝理3105 15%玻纤增强,阻燃