B4520 BK巴斯夫PBT-- B4520 BK00110 is a medium viscosity, pigmented black, rapidlyfreezing injection molding grade
B4520 BK00110是一种中等粘度、着色黑色、快速冷冻注射成型等级
PBT non reinforced resin has density of 1.3-1.45kg/cm3, hardnessof 85-90m, water absorption of 0.03-0.06%, molding shrinkage inflow direction of 0.8-2%, molding shrinkage in vertical directionof 1.2-2.2%, bending strength of 75-95mpa, notch impact of simplysupported beam (iso179) of 2-6, thermal deformation temperature(1.8MPa) of 50-75, thermal deformation temperature (0.45MPa) of130-163, melting point of 225 ℃,
PBT glass fiber reinforced resin has density of 1.37-1.78kg/cm3,hardness of 93-94m, water absorption of 0.03-0.04%, moldingshrinkage in flow direction of 0.1-0.6%, molding shrinkage invertical direction of 0.8-1.8%, bending strength of 160-260mpa,notch impact of simply supported beam (iso179) 4-16, thermaldeformation temperature of (1.8MPa) 200-214, thermal deformationtemperature of (0.45MPa) 220, melting point of 225 ℃,
PBT has high impact density of 1.37-1.78kg/cm3, hardness of93-94m, water absorption of 0.03-0.04%, molding shrinkage in flowdirection of 0.1-0.6%, molding shrinkage in vertical direction of0.8-1.8%, bending strength of 160-260mpa, notch impact of simplysupported beam (iso179) of 40-70, thermal deformation temperature(1.8MPa) of 200-214, thermal deformation temperature (0.45MPa) of220, melting point of 225 ℃,
PBT low warpage resin has density of 1.3-1.63kg/cm3, hardness of90-93m, water absorption of 0.03-0.06%, molding shrinkage in flowdirection of 0.1-0.5%, molding shrinkage in vertical direction of0.3-1.3%, bending strength of 90-200mpa, notch impact of simplysupported beam (iso179) of 2-10, thermal deformation temperature of110-210 (1.8MPa), thermal deformation temperature of 130-200(0.45MPa), melting point of 225 ℃,