15%玻纤增强美国杜邦PA66 HTN51G15HSL
Zytel? HTN51G15HSL BK083 is a 15% glass reinforced, heatstabilized, lubricated high performance polyamide resin. It is alsoa PPA resin.
Information provided by DuPont Performance Polymers
Polymer,Thermoplastic,Polyphthalamide (PPA),Polyphthalamide (PPA),20% Glass Fiber ReinforcedDuPont Performance PolymersDuPont Performance Polymers Zytel? HTN 51G15HSL BK083Polyphthalamide (PPA) (Unverified Data ) 物性表
物理性能额定值 (公制)额定值 (英制)测试方法比重1.31 g/cc1.31 g/ccDAM; ASTM D792密度1.30g/cc0.0470 lb/in3DAM; ISO 1183填料含量15 %15 %DAM线性成型收缩率0.0040 cm/cm@Thickness 1.60 mm
0.0040 in/in@Thickness 0.0630 in
Flow; DAM0.0045 cm/cm@Thickness 3.20 mm
0.0045 in/in@Thickness 0.126 in
Flow; DAM0.010 cm/cm
@Thickness 1.60 mm
0.010 in/in@Thickness 0.0630 in
Transverse; DAM0.011 cm/cm
@Thickness 3.20 mm
0.011 in/in@Thickness 0.126 in
Transverse; DAM线性成型收缩率,Flow0.0030 cm/cm
@Thickness 2.00 mm
0.0030 in/in@Thickness 0.0787 in
DAM; ISO 294-4线性成型收缩率，横向0.0060 cm/cm@Thickness 2.00 mm
0.0060 in/in@Thickness 0.0787 in
DAM; ISO 294-4机械性能额定值 (公制)额定值 (英制)测试方法抗张强度(断裂)110 MPa@Temperature 23.0 °C
16000 psi@Temperature 73.4 °F
DAM; ISO 527抗张强度123 MPa@Temperature 23.0 °C
17800 psi@Temperature 73.4 °F
DAM; ASTM D638伸长率 (断裂)2.0 %@Temperature 23.0 °C
2.0 %@Temperature 73.4 °F
DAM; ASTM D6382.0 %@Temperature 23.0 °C
DAM; ISO 527拉伸模量6.50 GPa
@Temperature 23.0 °C
943 ksi@Temperature 73.4 °F
DAM; ISO 527弯曲强度162 MPa@Temperature 23.0 °C
23500 psi@Temperature 73.4 °F
DAM; ASTM D790弯曲模量5.80 GPa@Temperature 23.0 °C
841 ksi@Temperature 73.4 °F
DAM; ISO 1786.21 GPa@Temperature 23.0 °C
901 ksi@Temperature 73.4 °F
DAM; ASTM D790悬壁梁缺口冲击强度0.530 J/cm
@Temperature 23.0 °C
0.993 ft-lb/in@Temperature 73.4 °F
DAM; ASTM D2565.00 kJ/m2@Temperature -40.0 °C
2.38 ft-lb/in2@Temperature -40.0 °F
DAM; ISO 180/1A5.00 kJ/m2
@Temperature 23.0 °C
2.38 ft-lb/in2@Temperature 73.4 °F
DAM; ISO 180/1A简支梁无缺口冲击强度2.30 J/cm2
@Temperature 23.0 °C
10.9 ft-lb/in2@Temperature 73.4 °F
DAM; ISO 179/1eU简支梁缺口冲击强度0.500 J/cm2@Temperature -40.0 °C
DAM; ISO 179/1eA0.500 J/cm2@Temperature 23.0 °C
DAM; ISO 179/1eA电气性能额定值 (公制)额定值 (英制)测试方法体积电阻率1.00e+15 ohm-cm
@Temperature 23.0 °C
1.00e+15 ohm-cm@Temperature 73.4 °F
DAM; IEC 60093表面电阻1.00e+16 ohm@Temperature 23.0 °C
1.00e+16 ohm@Temperature 73.4 °F
DAM; IEC 60093介电常数3.7@Frequency 1.00e+6 Hz, Temperature 23.0 °C
3.7@Frequency 1.00e+6 Hz, Temperature 73.4 °F
DAM; IEC 602504.0@Frequency 1000 Hz, Temperature 23.0 °C
4.0@Frequency 1000 Hz, Temperature 73.4 °F
DAM; IEC 60250介电强度16.5 kV/mm
@Temperature 23.0 °C
419 kV/in@Temperature 73.4 °F
DAM; IEC 60243-1耗散因数0.015@Frequency 1000 Hz, Temperature 23.0 °C
0.015@Frequency 1000 Hz, Temperature 73.4 °F
DAM; IEC 602500.018@Frequency 1.00e+6 Hz, Temperature 23.0 °C
0.018@Frequency 1.00e+6 Hz, Temperature 73.4 °F
DAM; IEC 60250Comparative Tracking Index575 V
@Temperature 23.0 °C
575 V@Temperature 73.4 °F
DAM; IEC 60112575 V@Temperature 23.0 °C
DAM; UL 746A热性能额定值 (公制)额定值 (英制)测试方法熔融温度300 °C572 °F10°C/min, First Heat; DAM;ISO 11357-1/-3300 °C572 °FDAM; ASTM D3418
载荷下热变形温度(0.46 MPa)276 °C529 °FDAM; ISO 75-1/-2载荷下热变形温度(1.8 MPa)245°C473 °FDAM; ASTM D648250 °C482 °FDAM; ISO 75-1/-2
UL RTI150 °C
@Thickness 3.00 mm
302 °F@Thickness 0.118 in
DAM; UL 746B150 °C@Thickness 0.750 mm
302 °F@Thickness 0.0295 in
DAM; UL 746B150 °C
@Thickness 1.50 mm
302 °F@Thickness 0.0591 in
DAM; UL 746BUL RTI，机械冲击125 °C
@Thickness 0.750 mm
257 °F@Thickness 0.0295 in
DAM; UL 746B125 °C@Thickness 1.50 mm
257 °F@Thickness 0.0591 in
DAM; UL 746B130 °C
@Thickness 3.00 mm
266 °F@Thickness 0.118 in
DAM; UL 746BUL RTI，机械无冲击130 °C
@Thickness 0.750 mm
266 °F@Thickness 0.0295 in
DAM; UL 746B140 °C@Thickness 1.50 mm
284 °F@Thickness 0.0591 in
DAM; UL 746B150 °C
@Thickness 3.00 mm
DAM; UL 746B可燃性(UL94)HB
@Thickness 0.750 mm
HB@Thickness 0.0295 in
DAM; IEC 60695-11-10HB@Thickness 1.50 mm
HB@Thickness 0.0591 in
DAM; IEC 60695-11-10HB
@Thickness 3.00 mm
HB@Thickness 0.118 in
DAM; UL94HB
@Thickness 1.50 mm
DAM; UL94HB
@Thickness 0.750 mm
DAM; UL94极限氧指数23 %23 %DAM; ISO 4589-1/-2加工性能额定值 (公制)额定值 (英制)测试方法加工（熔体）温度325°C617 °FDAM; Optimum320 - 330 °C608 - 626 °FDAM
模具温度150 °C302 °FDAM; optimum140 - 160 °C284 - 320 °FDAM
干燥温度100 °C212 °FDAM干燥时间6.00 - 8.00 hour6.00 - 8.00 hourDAM水分含量=0.10 %= 0.10 %DAM材料描述测试方法
外观Black ColorDAMDrying RecommendedYes, if moisture content of resinexceeds recommended levelDAMFillerGlass FiberreinforcementDAM形式PelletsDAMGenericPolyphthalamide (PPA)DAMHeatStabilizedYesDAMMaterial StatusCurrentDAM部件标识代码PA6T/XT-GF15ISO11469; DAMPPA-GF15SAE J1344; DAM
Polymer FamilyHigh performance polyamideDAMPolymer TypePartiallyAromatic PA, PPADAM加工方法Injection MoldingDAM产品分类Glass ReinforcedResinsDAMRegion Available - GlobalYesDAM树脂识别PA6T/XT-GF15ISO 1043;DAM符合RoHS指令Contact ManufacturerDAMUltrasonic WeldableYesDAM
15%玻纤增强美国杜邦PA66 HTN51G15HSL