| 线性热膨胀系数,横向流动 | 90.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 50.0 µin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ASTM E 831 |
| 90.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 50.0 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | |
| 90.0 µm/m-°C @Temperature -30.0 - 30.0 °C | DAM; ISO 11359-1/-2 | ||
| 90.0 µm/m-°C @Temperature -40.0 - 23.0 °C | DAM; ISO 11359-1/-2 | ||
| 100 µm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |
| 100 µm/m-°C @Temperature 23.0 - 55.0 °C | DAM; ISO 11359-1/-2 | ||
| 130 µm/m-°C @Temperature 55.0 - 160 °C | 72.2 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |
| 130 µm/m-°C @Temperature 55.0 - 160 °C | DAM; ISO 11359-1/-2 | ||
| 熔融温度 | 260 °C | 500 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| 载荷下热变形温度(1.8 MPa) | 65.0 °C | 149 °F | DAM; ISO 75-1/-2 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 290 °C | 554 °F | DAM; Optimum |
| 280 - 300 °C | 536 - 572 °F | DAM | |
| 模具温度 | 70.0 °C | 158 °F | DAM; optimum |